在前人研究Q相合成基础上,采用正交实验的方法,研究了Q相-CA-C12A7体系水泥的烧成条件及水化性能.研究结果表明:在Q相-CA-C12A7系统中,Q相的形成温度在1260～1340℃之间;Q相-CA-C12A7系统水泥烧成的最佳条件是温度为1320℃,保温时间为40min.此水泥具有早期强度高,中期强度提高快,后期强度不发生倒缩.
参考文献
| [1] | Glasser F P;Marr J .Quaternary phase in the system CaO-MgOAl2O3-SiO2[J].Transactions Journal of the British Ceramic Society,1975,74:113-119. |
| [2] | Kapralik I;Hanic F .Studies of the system CaO-MgOAl2O3-SiO2 in relation to the quaternary phase Q[J].Transactions Journal of the British Ceramic Society,1980,79:128-133. |
| [3] | Aknmetov I S;Mlryuk O A.Phase transformation when synthesizing clinkers produced of technogeneous rew materials[A].India,1992:74-80. |
| [4] | 姜奉华;杨利群;徐先宇 .Q相-CA-C1 2A7系列水泥烧成条件的研究[J].山东建材学院学报,1998,12(04):352-355. |
| [5] | E. Dourdounis;V. Stivanakis;G.N. Angelopoulos .High-alumina cement production from FeNi-ERF slag, limestone and diasporic bauxite[J].Cement and Concrete Research,2004(6):941-947. |
| [6] | Scrivenet K L;Cbairon J L .High-performance concretes from calcium alumina cement[J].Cement and Concrete Research,1999,29:1215-1223. |
| [7] | Kapralik I;Stevula L;Hanic F .Hydration and hydraulic properties of the Q-phase in the system CaO-MgO-Al2O3-SiO2-H2O referred to high-alumina cement[J].Cement and Concrete Research,1989,19:519-526. |
| [8] | Lea F M.The Chemistry of Cement and Concrete[M].London:Edward Arnold,1970 |
| [9] | 姜奉华,郑少华.高铝水泥系统中硅铝酸二钙向Q相的转变[J].硅酸盐学报,2005(04):462-466. |
| [10] | 姜奉华.Q相-C2S-C4AF-C12A7系列水泥水化性能的研究[J].济南大学学报(自然科学版),2004(03):192-193. |
| [11] | 姜奉华,徐德龙,郑少华.新型Q相高铝水泥的烧成条件[J].硅酸盐学报,2004(10):1289-1292. |
| [12] | 姜奉华.Q相-CA-C12A7高铝水泥烧成的正交试验研究[J].济南大学学报（自然科学版）,2005(01):21-24. |