采用差热分析(DTA)、场发射扫描电镜、X射线衍射仪(XRD)等材料显微结构的分析手段以及一些力学性能测试方法,分析了CaO-MgO-P2O5-SiO2系微晶玻璃的显微组织形貌与其力学性能之间的关系.结果表明:对试样在810℃进行4h的保温处理后,该试样具有较细的晶粒和比较紧凑的显微结构.因此,经过这种处理的微晶玻璃具有较好的抗弯强度和较高的断裂韧性.
参考文献
| [1] | Salinas AJ;Roman J;Vallet Regi-M;Oliveira JM;Correia RN;Fernandes MH .In vitro bioactivity of glass and glass-ceramics of the 3CaO x P2O5-CaO x SiO2-CaO x MgO x 2SiO2 system.[J].Biomaterials,2000(3):251-257. |
| [2] | Hench L L;Splinter R J;Allen W C et al.Bonding mechanisms at the interface of ceramic prosthetic materials[J].Journal of Biomedical Materials Research Symposium,1971,2:117-141. |
| [3] | Chyung K;Beall G H;Grossman D G .Fluorophlogopite mica glass-ceramics[J].Avtomaticheskaya Svarka,1974,7:8-12. |
| [4] | Beall G H .Microstructure of glass ceramics and photosensitive glasses[J].Glass Technology,1978,19(10):109-113. |
| [5] | Hoeland W;Naumann K;Vogel W .Machinable,bioactive glass ceramics material[P].DE 3306648A,1983. |
| [6] | 朱光明;黄占杰 .可切削生物活性玻璃陶瓷的研制[J].硅酸盐学报,1988,16:416-421. |
| [7] | 罗谰;李家治 .生物微晶玻璃及其用途[P].CN:1035999,1989. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%