利用电沉积技术在45钢表面制备了Ni-W-Co-B4C复合镀层,并研究了油润滑磨损条件下Ni-W-Co-B4C复合镀层的磨损特性.结果表明,Ni-W-Co镀层磨损形貌中有很深的犁沟,局部并有黏着磨损的特征,镀层的抗磨损性能较差;加入B4C颗粒的Ni-W-Co-B4C复合镀层磨损形貌试验中的犁沟较浅,没有发现黏着磨损现象,但B4C颗粒与金属基体结合不牢,有颗粒脱落现象.B4C颗粒含量、大小和载荷都对复合镀层的耐磨性有影响.当镀层中含有20%(体积分数)的B4C颗粒时,磨损性能最好.
参考文献
| [1] | Greco V P .A Review of Fabrication and Properties of Electrocomposites[J].Plating and Surface Finishing,1989,76(07):62-67. |
| [2] | C. R. Lin;C. T. Kuo .Improvement of mechanical properties of electroplated diamond tools by microwave plasma CVD diamond process[J].Surface & Coatings Technology,1998(1/2):19-23. |
| [3] | Zhang Z;Zhang L;Mai Y W .Modeling steady wear of steel/Al2O3-Al particle reinforced composite system[J].Wear,1997,211(02):147-150. |
| [4] | 张三元.室温电沉积Fe-B4C复合镀层的某些研究[J].电镀与精饰,1989(03):18. |
| [5] | 董允,林晓娉,邵荷生,曲敬信.Ni-W-Co/SiC复合材料磨损特性与磨损机制[J].摩擦学学报,1999(01):12-17. |
| [6] | Thevenot F.Boron Carbon--A Comprehensive Review[J].Journal of the European Ceramic Society,1990(06):205-225. |
| [7] | 张会臣;郭鹤桐 .电沉积Ni-P-Si3Ni4复合镀层的摩擦学特性[J].天津大学学报,1997,30(03):245-251. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%