探讨了Ag-Fe3O4磁性导电复合粉末的制备方法及工艺条件.研究表明,采用超声波振荡分散,在镀液pH=10~12,反应时间≥60 min,适当的Fe3O4用量下可以制备出粉末表面Ag:Fe摩尔比为55.17:37.84、具备Ag-Fe3O4壳-核结构且导电性良好的磁粉材料.此外,还借助扫描电镜、EDS能谱分析仪及电学测量等方法对粉体材料的表面形貌、化学组成和导电性进行了分析和评估.
参考文献
[1] | W-S. Chung;S-Y. Chang;S-J. Lin .Electroless Nickel Plating on SiC Powder with Hypophosphite as a Reducing Agent[J].Plating & Surface Finishing,1996(3):68-71. |
[2] | S.Y.Chang;J.H.Lin .Processing copper and silver matrix composites by electroless plating and hot pressing[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1999(4):1119-1136. |
[3] | Zhang C;Ling G P;He J H .Co-Al2O3 nanocomposites powder prepared by electroless plating[J].Materials Letters,2003,58:200-204. |
[4] | 黄磊,凌国平,郦剑.纳米Ag-Al2O3复合粉末的制备[J].浙江大学学报(工学版),2003(01):65-69. |
[5] | Fitzer E .Lecture at the Institute of Metal Research,Academia Sinica[R].Shenyang:Institute of Metal Research Chinese Academy of Science,1988. |
[6] | Warrier S G;Lin R Y .Silver Coating on Carbon and SiC Firbers[J].Journal of Materials Science,1993,28(18):4868-4877. |
[7] | 赵择卿.高分子材料抗静电技术[M].北京:纺织工业出版社,1991 |
[8] | 黄少强,邱文革,陈江涛.非金属粉体化学镀银影响因素的研究[J].材料保护,2004(10):23-25. |
[9] | 赵文轸.材料表面工程导论[M].西安:西安交通大学出版社,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%