研究了微弧氧化陶瓷层粗糙度对磨损特性的影响及在不同溶液添加剂中生成的铝合金微弧氧化陶瓷层的磨损特性,并与镀硬铬及耐磨磷钒铜铸铁的磨损特性进行了对比.试验结果表明:随着微弧氧化陶瓷层粗糙度的增大,其初期磨损量较大,当磨损一定时间后,其磨损失重量接近于零;溶液添加剂对陶瓷层的磨损特性没有明显的影响;微弧氧化陶瓷层的磨损特性明显优于镀硬铬及磷钒铜耐磨铸铁.
参考文献
| [1] | TucciA;Esposito L .MicrostructureandtribologicalpropertiesofZrO2ceramics[J].WEAR,1994,172:111-119. |
| [2] | DiavakerR .Siteredsiliconcarbidewithcontrolledporosityformechanicalfacesealalications[J].Lubrication Engineering,1994,50:75-80. |
| [3] | AjayiO;Ludema K C .Theeffectofmicrostructureonwearofceramicmaterials[J].Wear,1992,154:371-385. |
| [4] | Wallis .Influenceofthemicrostructureofceramicmaterialsontheirwearbehaviorinmechanicalseals[J].Lubrication Engineering,1994,50:789-799. |
| [5] | 薛文彬,邓志威,来永春.LY12铝合金微弧氧化的尺寸变化规律[J].中国有色金属学报,1997(03):140-143. |
| [6] | MarkovGA;Markova G V .The formation method of anodic electrolytic condensation[P].SU Pat: 526961,1976. |
| [7] | NikolacvAV;Markov G A;Peshchevitskii B I.Anewphenomenonelectrolysis[J].Izvestiya Akademii Nauk SSSR Seriya Khimicheskaya,1977(05):32. |
| [8] | KurzeP;Krysmann H G .ApplicationfieldsofANOFlayersandcomposites[J].Crystal Research and Technology,1986,21(12):1603. |
| [9] | 柳田和夫 .Ceramicsfilmsonaluminumbyelectrolyticdepositionprocess[J].ァルトヒァ,1987,17(04):49. |
| [10] | 刘凤岭.微弧氧化与材料表面陶瓷化[J].材料保护,1998(03):22. |
| [11] | 贺子凯,唐培松.溶液体系对微弧氧化陶瓷膜的影响[J].材料保护,2001(11):12-13. |
| [12] | 李溪滨,刘如铁,程时和,李美英.烧结材料中孔隙度对摩擦学特性的影响[J].润滑与密封,2002(01):34-35. |
| [13] | 蒋百灵,吴国建,张淑芬,雷廷权.镁合金微弧氧化陶瓷层生长过程及微观结构的研究[J].材料热处理学报,2002(01):5-7. |
| [14] | 邵荷生;曲敬信.摩擦与磨损[M].北京:煤炭工业出版社,1992:98. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%