利用电化学方法探讨了在电镀镉及加入Al2O3微粒过程中,Al2O3微粒的加入量对其氢渗入量的影响.试验表明:在其过程中,夹杂Al2O3微粒可以减少氢的渗入量,且随着夹杂到镀层中Al2O3微粒的增加,渗入到基体金属的氢量减少;同时还发现,渗氢电流均是由突峰到稳定,一段时间后再以较快的速度上升,然后缓慢平稳.
参考文献
| [1] | 沈宁一.表面处理技术手册[M].上海:上海科学技术出版社,1993 |
| [2] | 曾华梁;吴仲达;陈钧武.电镀工艺手册[M].北京:机械工业出版社,2002 |
| [3] | Kudryavtsev N .Investigation of Steel Hydrogenation During Cadmium from Cyanide Solutions and Some Questions Connected with Hydrogen Embittlement Elimination-[J].Transactions of the Institute of Metal Finishing,1972,50:223. |
| [4] | 谢春福;吴忠利;张凤珍.镀锌时渗氢量的测定[J].兵工学报-防腐与包装分册,1980(02):1-8. |
| [5] | Minoru Hiratsu;Eiichi Sukedai;Hitoshi Kawasaki et al.Hydrogen Embrittlement Behavior of Zinc Electroplated High Strength Steel and the Effects of Silica Codeposition-[J].The Journal of the Metal Finishing Society of Japan,1988,39(07):52-57. |
| [6] | Nobukazu SUZUKI;Nobuyuki ISHII .Diffusible Hydrogen Behavior and Delayed Fracture of Zinc-electrogalvanized High Strength Steel[J].鉄と鋼,1996(2):72-77. |
| [7] | 曹江利,吴继勋,卢燕平,杨玲莉,郑建平.Zn-SiO2复合镀中氢的侵入及镀后逸出行为[J].材料保护,2000(04):8-9. |
| [8] | Pushpavanam M;Shenoi B A .Nickel-Aluminum Oxide Composite Coatings[J].Metal Finishing,1977,75(04):38-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%