分析了我厂银币表面缺陷形成的原因,并提出了在银币表面施加保护膜的设想,通过各种防变色工艺实验,提出了采用电解保护和浸渍抗变色剂的多层组合防护膜保护工艺方案.实验表明,经过该保护工艺处理的银币自然放置半年无白斑及其他变色现象产生,在40 ℃,3 mg/L硫化氢气体和3%硫化钾溶液中耐蚀时间为130 min,分别为未经处理银币的耐蚀时间的10倍和26倍.
参考文献
[1] | 唐致远,郭鹤桐,于英浩.防银变色及其机理的研究[J].电镀与精饰,1999(03):9-12. |
[2] | 方景礼.银层光照和Na2S处理致变色的机理[J].电镀与精饰,1985(04):8. |
[3] | Dick L F P .The mechanism of tarnishing of silver and silver-gold alloys in hydrogen sulfide/water-bearing atmospheres[J].Proceedings-Electrochemical Society,1991,91(02):273-283. |
[4] | 蒋勇 .镀银层防变色工艺[J].电镀与涂饰,1996,15(04):38. |
[5] | 白鸿生.防银层变色新工艺试验[J].电镀与精饰,1988(04):26. |
[6] | 关颖中.镀银层抗变色能力试验[J].电镀与精饰,1999(01):24-26. |
[7] | 田开尚.镀银件防变色处理工艺对比试验[J].电镀与精饰,1992(05):20. |
[8] | 田开尚.镀银件防变色处理工艺对比试验[J].电镀与精饰,1992(05):20. |
[9] | 梁时骏.防银变色的工艺现状及设想[J].电镀与精饰,1991(02):19. |
[10] | 宝根 .镀银件腐蚀变色及保护[J].电镀与涂饰,1998,17(04):30. |
[11] | [P].London Patent,1308391 |
[12] | [P].US RE |
[13] | [P].German 1116216 |
[14] | [P].German Pat 1243808 |
[15] | [P].German Pat 1279428 |
[16] | 陈春成 .防银变色技术的概况及发展趋势[J].电镀与环保,1999,19(01):3. |
[17] | 杨洗.推荐一种防银变色处理工艺[J].电镀与精饰,1996(02):28. |
[18] | 曾华梁.电镀工艺手册[M].北京:机械工业出版社,1997 |
[19] | 许绍杰.EC2000阴极电泳漆[J].电镀与精饰,1992(02):30. |
[20] | Dick L F P.The tarnishing of silver sand silver-gold alloys in aqueous sulfide solutions and in hydrogen sulfide[J].Proceedings-Electrochemical Society,1993(01):406. |
[21] | Saber T M H .AES and XPS study on the tarnishing of silver in alkaline sulfide solutions[J].Journal of Materials Science,1988,23(04):1496-1501. |
[22] | Kovacs G J .Sulfide formation on evaporated silver films[J].Surface Science Spectra,1978,78(01):245-249. |
[23] | Feinstein H I .Instant silver tarnish-detarnish[J].Journal of Chemical Education,1976,53(01):34. |
[24] | Burge D K .Effect of atmospheric exposure on the infrared reflectance of silvered mirrors with and without protective coatings[J].Applied Optics,1973,12(01):42-47. |
[25] | BENNETT H .Formation and growth of tarnish on evaporated silver films[J].Journal of Applied Physics,1969,40(08):3351-3360. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%