连铸坯厚度中心存在的内裂纹在后续的轧制过程中轧不合而对产品的质量带来重大的影响.笔者通过使用电子探针等设备对含铌包晶钢的连铸坯边部三角区内的裂纹进行了研究,在裂纹的表面发现了富铌的共晶体.
参考文献
| [1] | 牛宏波;刁承民;宋宜华 .SS400钢板坯三角区裂纹和中心裂纹成因及预防[J].山东冶金,1999,21:110-112. |
| [2] | Fujii H;Ohashi T;Hiromoto T.On the Formation of Internal Cracks in Continuously Cast Slabs[J].Transactions of the Iron and Steel Institute of Japan,1978:510-518. |
| [3] | Yamauchi N;Uchida Y;Yamamoto T.Internal Cracks in Continuously[J].Cast Slabs Nippon Steel Technical Report,1979:62-72. |
| [4] | Matsumiya T;Ito M;Kajioka H.An Evaluation of Critical Strain for Internal Crack Formation in Continuously Cast Slabs[J].Transactions of the Iron and Steel Institute of Japan,1986:540-546. |
| [5] | 韩志强;袁伟霞.连铸板坯内裂纹的形成与防止[J].连铸,1999(06):10-15. |
| [6] | Chong Hee YU;Mikio SUZUKI;Hiroyuki SHIBATA;Toshihiko EMI .Simulation of Crack Formation on Solidifying Steel Shell in Continuous Casting Mold[J].ISIJ International,1996(1):S159-S162. |
| [7] | Makoto Naitou Shigenobu Takata.High Speed Casting Technology by Analysis and Prevention of Internal Cracks in Slabs at the Continuous Caster[A].,1999:79-87. |
| [8] | Won Y. M.;Yeo T.-J. .A New Criterion for Internal Crack Formation in Continuously Cast Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(4):779-794. |
| [9] | Cornelissen M C M .Mathematical Model for Solidification of Multicomponent Alloys[J].Ironmaking and Steelmaking,1986,13:204. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%