采用Czochralski法生长了透明均匀的Cr:Nd:YCaO(BO3)3晶体,生长的晶体尺寸为φ42.5×50mm,生长参数为提拉速度为0.6mm/h,转速为25r/min.测定了其室温吸收谱.根据Judd-Ofelt理论拟合了Nd3+离子的强度参数Ωλ:Ω2=0.734×10-20,Ω4=6.814×10-20,Ω6=2.476×10-20;并计算了各能级跃迁的自发辐射跃迁几率、辐射寿命、荧光分支比.其中4F3/2能级的寿命τtot=271.64μs,4F3/2→4I9/2的荧光分支比βc=58.01%.并对实验结果进行了讨论.
参考文献
| [1] | Aka G;Bloch L;Bentez J M et al.A New Nonlinear Oxoborate Crystal,Characterized by Using Femtosecond Broadband Pulses,OSA TOPS on Advanced Solid Laser[Z].,1996. |
| [2] | Iwai M;Kobayashi T;Turuya H et al.Crystal Growth and Optical Characterization of Rare-earth (Re) Calcium Oxyborate ReCa4O(BO3)3 as New Nonlinear Optical Materials[J].Japanese Journal of Applied Physics,1997,36:L276. |
| [3] | 宫波,魏景谦,王继扬,刘耀岗,胡晓波,管庆才,蒋民华.高质量YCOB和Nd：YCOB晶体的生长条件探讨[J].人工晶体学报,1999(01):31-36. |
| [4] | Kaminskii A A.Laser Crystal Springer-verlag Berlin[M].Heidelberg,Germany,1981:154. |
| [5] | Mougel F;Aka G;Kahn-Harari A .Infrared Laser Performance and Self-frequency Doubling of Nd3+:Ca4GdO(BO3)3(Nd:GdCOB)[J].Optical Materials,1997,8:161-173. |
| [6] | Ofelt G S .Intensities of Grystal Spectra of Rare-earth Ions[J].Journal of Chemical Physics,1962,37:511-520. |
| [7] | 吕军华 .低对称自倍频晶体Nd:ReCRB(Re=Y,Gd)各向异性的研究[D].山东大学,1999. |
| [8] | Ye Q.;Chai BHT. .Crystal growth of YCa4O(BO3)(3) and its orientation[J].Journal of Crystal Growth,1999(1/2):228-235. |
| [9] | Zhang Shujun;Cheng Zhenxiang;Zhou Guangyong.Growth and Properties of (Cr3+,Nd3+)Doped GdCa4O(BO3)3 Crystals[A].Beijing:Chinese Material Research Society,1999:537. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%