采用四点弯曲试样在高频疲劳试验机上对铝基复合层板进行了疲劳试验,采用直流电势法测量裂纹长度,用扫描电镜和光学显微镜观察其疲劳断口及疲劳裂纹形貌,通过对比性试验,考察了组元性能错配和界面结合强度对复合板L-T取向疲劳裂纹扩展行为的影响,并用断裂力学理论对其进行了初步分析.结果表明:性能错配的复合双层板两侧面的疲劳裂纹扩展通过界面产生牵扯作用,扩展速率相对于整体材料发生变化,近似符合混和定则;界面对层合板L-T取向疲劳性能的韧化作用以分层韧化为主,结合强度不同,产生的影响也不一样.
参考文献
| [1] | 王人杰;罗海安 .具有理想与非理想界面的双材料四点弯曲试件的界面断裂韧性[J].复合材料学报,1996,13(04):58-63. |
| [2] | 王惠军;杨卫 .材料不均匀层对垂直裂纹的作用[J].复合材料学报,1996,13(01):91-95. |
| [3] | Woeltjen C;Shih C F;Suresh S .Cyclic near-tip fields for fatigue cracks along metal-metal and metal-ceramic interfaces[J].ACTA METALLURGICA ET MATERIALIA,1993,41(08):2317-2335. |
| [4] | Rica J R .Elastic fracture mechanics concepts for interfacial cracks[J].Journal of Applied Mechanics,Transactions of the ASME,1988,55:98-103. |
| [5] | He Ming-yuan;John W Hutchinson .Crack deflection at an interface between dissimilar elastic materials[J].Journal of Solids Structure,1989,25(09):1053-1067. |
| [6] | Schijve J;Van Lipzig H T M;Van Gestel G F J A et al.Fatigue properties of adhesive-bonded laminated sheet material of aluminum alloys[J].Engineering Fracture Mechanics,1979,12(04):561-579. |
| [7] | 黄作宾.断裂力学基础[M].武汉:中国地质大学出版社,1991:91. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%