用Gleeble-3800热变形模拟试验机研究了锻态00Cr25Ni7Mo4N超级双相不锈钢在900~1 300 ℃时的高温拉伸塑性和高温变形组织特征.结果表明:温度对锻态超级双相不锈钢的热塑性影响显著,在1 100~1 200 ℃具有良好的热塑性,在1 200 ℃时断面收缩率最高达到70%,温度超过1 200 ℃后,热塑性下降明显;高温固溶处理对该不锈钢的热塑性有很大的影响,固溶处理温度为1 100 ℃时,热塑性提高.
参考文献
[1] | Park Y H;Lee Z H .The effect of nitrogen and heat treatment on the microstructure and tensile properties of 25Cr-7Ni-1.5N-3W-xN duplex stainless steel castings[J].Materials Science and Engineering,2001,A297(01):78-84. |
[2] | Iacoviello F;Casari F;Gialanella S .Effect of "475 ℃ embrittlement" on duplex stainless steels localized corrosion resistance[J].Corrosion Science,2005,47(04):909-922. |
[3] | T. MAKI;T. FURUHARA;K. TSUZAKI .Microstructure Development by Thermomechanical Processing in Duplex Stainless Steel[J].ISIJ International,2001(6):571-579. |
[4] | M.A. Ribeiro Miranda;J.M. Sasaki;S.S.M. Tavares .The use of X-ray diffraction, microscopy, and magnetic measurements for analysing microstructural features of a duplex stainless steel[J].Materials Characterization,2005(4/5):387-393. |
[5] | Cabrera J M;Mateo A;Llanes L et al.Hot deformation of dupleu stainless steels[J].Journal of Materials Processing Technology,2003,143-144(20):321-325. |
[6] | 吴玖.双相不锈钢[M].北京:冶金工业出版社,1999:2-4. |
[7] | L. DUPREZ;B.C. De COOMAN;N. AKDUT .Flow Stress and Ductility of Duplex Stainless Steel during High-Temperature Torsion Deformation[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2002(7):1931-1938. |
[8] | 《彩色金相技术》编写组.彩色金相技术(原理及方法)[M].北京:国防工业出版社,1987:119. |
[9] | Marcelo Martins;Luiz Carlos Casteletti .Heat treatment temperature Influence on ASTM A890 GR 6A super duplex stainless steel microstructure[J].Materials Characterization,2005(3):225-233. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%