对铬-镍-钼系重载齿轮钢进行钒-铌微合金化处理,并对比了微合金化处理前后的淬火与渗碳组织及其性能.结果表明:经过钒-铌微合金化处理后,该钢的奥氏体晶粒得到显著细化;伴随着晶粒的细化,其冲击吸收功得到较大幅度的提高;在渗碳温度范围内长时间保温时不会发生奥氏体晶粒的异常长大;晶粒细化也使其渗碳层的组织和性能得到改善.
参考文献
| [1] | 杨林,邵亮,乔兵,杜彩霞.含Nb齿轮钢晶粒度研究[J].汽车工艺与材料,2004(07):5-6. |
| [2] | 吴正锡.高强度渗碳齿轮钢17CrNiMo6的研究[J].四川冶金,1993(03):36-39. |
| [3] | Pacheco J L;Krauss G .Microstructure and high bending fatigue strength in carburized steel[J].Journal of Heat Treating,1989,7(02):77-86. |
| [4] | Wise J P;Matlock D K .Bending fatigue of carburized steels:A stastical analysis of process and microstructural parameters[J].SAE Transactions:Journal of Materials & Manufacturing,2000,109:182-191. |
| [5] | Stasko R;Adrian H;Adrian A .Effect of nitrogen and vanadium on austenite grain growth of a low alloy steel[J].Materials Characterization,2006,56(4-5):340-347. |
| [6] | Leap M J;Brown E L .Effect of composition and processing on development of grain coarsening resistance in cold forged and carburized steel[J].Materials Science and Technology,2002,18(09):945-958. |
| [7] | 王毛球,董瀚,王琪,李建新,赵隆.奥氏体化对3Cr-3Mo-Nb二次硬化钢的组织和力学性能的影响[J].兵器材料科学与工程,2002(05):9-13. |
| [8] | 项程云.合金结构钢[M].北京:冶金工业出版社,1999:384. |
| [9] | 王毛球,董瀚,王琪,李建新,赵隆.高强度炮钢的组织和力学性能[J].兵器材料科学与工程,2003(02):7-10,18. |
| [10] | 张银花,詹新伟,周清跃.CrNb低合金热轧轨组织和性能研究[J].铁道学报,2002(03):27-31. |
| [11] | Wang M Q;Zhang W H;Shi J.Microstructure and mechanical properties of V-Nb microalloyed steel for heavy duty gear[A].Korea:Gyeongiu,2006:411-415. |
| [12] | 董瀚.超细晶粒钢及其力学性能特征[J].中国冶金,2003(10):26-31,35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%