研究了长期时效对一种镍基单晶高温合金γ′相形貌的影响.结果表明:合金在950℃时效100h后,γ′相正方度略有下降,500h后γ′相开始沿不同的[100]方向长大.合金在1 050℃时效100h后,γ′相开始沿不同的[100]方向长大,长大速度明显高于950℃时效.γ/γ′相界面能和弹性应变能的降低是γ′相长大的驱动力,γ′相按 Ostwald熟化方式长大,即大的γ′相长大,小的γ′相溶解,高温长期时效过程中无有害相析出,表明合金的组织是稳定的.
参考文献
| [1] | Tawancy H M .The Microstructure thermal stability of a nickel-base superalloy[J].Journal of Maer Sci,1983,18:2976. |
| [2] | Lai G Y .An investigation of the thermal stability of a cummercial Ni-Cr-Fe-Mo alloy (Hastelloy alloyx)[J].Metallurgical and Materials Transactions,1978,9(09):827. |
| [3] | 王淑荷;郭建亭;赖万慧 等.GH903高温合金650℃长期时效后的组织与性能[J].金属学报,1990,26(06):A432. |
| [4] | 姜文辉;姚向东;管恒荣 等.DZ40M钴基高温合金950℃长期时效后的组织与性能[J].金属学报,1998,34(12):1289. |
| [5] | Khachzturyan A G;Semennovskaya S V;Morris J W .Sci.Theoretical analysis of strain-induced shape changes in cubic precipitates during coarsening[J].Acta Materialia,1988,36:1563. |
| [6] | Mulier L;Glatzedl U;Feller Kniepmeier M .Modelling thermal misfit stresses in nickel-base superalloys containing high volume fraction[J].Acta Metallurgica Et Materialia,1992,40(06):1321. |
| [7] | Glatzedl U;Feller-Kniepmeier M .Calculations of internal stresses in the γ/γ′ microstructure of a nickel-base superalloy with high fraction of γ′ phase[J].Scripta Metallurgica et Materialia,1989,23:1839. |
| [8] | 任英磊,金涛,管恒荣,胡壮麒.热处理制度对一种单晶镍基高温合金γ′相形貌演化的影响[J].机械工程材料,2001(04):7-10. |
| [9] | 田素贵 .单晶镍基合金组织演化与蠕变行为及微观特征的研究[D].东北大学,1998. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%