利用共沉淀法制备了纳米多晶La2/3Sr1/3MnO3粉体,并研究了相应烧结陶瓷的相结构、显微形貌、电性质以及磁电阻效应.样品中存在高密的晶界,对电子的疏运过程产生明显的散射作用,从而使得样品具有较大的电阻值,并且只有当烧结温度大于800℃时才出现金属绝缘体温度相变.样品的磁电阻是低场磁电阻效应,源于晶界处电子的自旋极化隧穿.烧结温度越低的样品,其磁电阻越大.
参考文献
[1] | von Helmolt R;Wecker J;Holzapfel B;Schultz L and Samwer K .[J].Physical Review Letters,1993,71:2331. |
[2] | P K Siwach;U K Goutam;Pankaj Srivastava;H K Singh,R S Tiwari and O N Srivastava .[J].Journal of Physics D:Applied Physics,2006,39:14. |
[3] | Mahesh R;Mahendiran R;Raychaudhuri A K;Rao C N R .[J].Applied Physics Letters,1996,68:2291. |
[4] | A VADIVEL MURUGAN;A B GAIKWAD;V SAMUEL;V RAVI Bull .[J].Materials Science,2006,29:221. |
[5] | 席力,杨啸林,李成贤,葛世慧.纳米多晶La0.7Sr0.3MnO3-δ的输运性质和磁电阻效应研究[J].物理学报,2006(02):854-859. |
[6] | Hwang Y H;Cheong S W;Ong N P;Batlogg B .[J].Physical Review Letters,1996,77:2041. |
[7] | Hueso LE.;Rivadulla F.;Lopez-Quintela MA.;Rivas J. .Magnetoresistance in manganite/alumina nanocrystalline composites[J].Journal of Applied Physics,2001(3):1746-1750. |
[8] | Yuan X;Liu Y;Yin N;Wang C and Mei L .[J].Journal of Physics D:Applied Physics,2006,39:1028. |
[9] | Anulekha Durra;N Gayathri;R Ranganathan .[J].Physical Review B,2003,68:054432. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%