本文研究了La1-xNaxMnO3和La1-xAgxMnO3结构、磁性、电输运等.特别是研究了La0.8Na0.2MnO3的内耗特性.XRD研究发现La1-xNaxMnO3和La1-xAgxMnO3的结构均为R3C,但是不同的是对于La1-xAgxMnO3,当x>0.25时有Ag单质吸出.从磁化强度随温度的变化看出所有的样品都在室温或室温以上有顺磁到铁磁的转变,而且随着掺杂量的增加,居里温度也在增加.电输运研究发现对于La1-xNaxMnO3,x=0.15的电阻率最小,随掺杂量增大电阻率增大;x≥0.15的样品中存在电阻双峰.而对于La1-xAgxMnO3电阻率随掺杂量增加而减小;x<0.2的样品中存在电阻双峰.在La0.8Na0.2MnO3的内耗测量中发现了具有相变峰特征的内耗双峰.我们认为这种电阻双峰和内耗双峰来源于样品中存在A位空位,导致了样品中存在电子相和磁相的不均匀,即相分离.就是在样品存在着铁磁相和反铁磁相共存.
参考文献
| [1] | J H Van Santen;G H Jonker .[J].Physica,1950,16:599. |
| [2] | C Zener .[J].Physical Review,1951,82:403. |
| [3] | J Volger .[J].Physica,1954,20:49. |
| [4] | S Jin;H Tiefel;M Mecormack et al.[J].Science,1994,264:413. |
| [5] | R Von Helmolt;J Wecker;B Holzapfel et al.[J].Physical Review Letters,1993,71:2331. |
| [6] | S Yunoki et al.[J].Physical Review Letters,1998,81:5612. |
| [7] | A J Millis;P B Littlewood;B I Shraiman .[J].Physical Review Letters,1995,74:5144. |
| [8] | T. Tao;Q. Q. Cao;K. M. Gu .Giant magnetoresistance of the La_(1-x)Ag_(x)MnO_(3) polycrystalline inhomogeneous granular system[J].Applied physics letters,2000(5):723-725. |
| [9] | Li X.-G.;Fan X.J.;Ji G.;Wu W.B.;Wong K.H.;Choy C.L.;Ku H.C. .Field-induced crossover from cluster-glass to ferromagnetic state in La_(0.7)Sr_(0.3)Mn_(0.7)Co_(0.3) O_3[J].Journal of Applied Physics,1999(3):1663-0. |
| [10] | J M D Coey;M Viret;L Ranno .[J].Physical Review Letters,1995,75:3910. |
| [11] | J. R. Sun;G. H. Rao;J. K. Liang .Crystal structure and electronic transport property of perovskite manganese Oxides with a fixed tolerance factor[J].Applied physics letters,1997(13/16):1900-1902. |
| [12] | G H Rao;J R Sun;J K Liang;W Y Zhou .[J].Physical Review B,1997,55:3742. |
| [13] | J Alonso;E Herreo;J M Gonzalez-Calbet;M Vallet-Regi,J L Martinez,J M Rojo,and A Hermando .[J].Physical Review B,2000,62:11328. |
| [14] | 谢津桥,吴鸿毅,苏金瑞,钱天,朱长飞.La0.9Na0.1MnO3的反常超声特性[J].低温物理学报,2002(04):298-302. |
| [15] | G T Wang;Q F Fang .[J].Physica Status Solidi,2002,191:260. |
| [16] | Das S;Poddar A;Roy B;Giri S .[J].Journal of Alloys and Compounds,2004,365:94. |
| [17] | Fan Rui;Zhao Yong-gang;Zhang Xiao-ping;Sun Tao,Cao Bi-song .[J].Chin J Low Temp Phys,2002,24(04):291. |
| [18] | 李拥军,方军,黄真,刘智民,高秉钧.双层钙钛矿锰氧化物La1.4（Ca1-xSrx）1.6Mn2O7的制备工艺对材料结构和性能的影响[J].低温物理学报,2002(03):203-207. |
| [19] | Zhu CF;Zheng RK;Zhang JH;Li XG,Su JR,Zhu ZG .[J].Journal of Alloys and Compounds,2000,310:59. |
| [20] | 冯端.金属物理学第三卷金属力学性质[M].北京:科学出版社,1999:170,196. |
| [21] | 任清褒;张裕恒 .[J].低温物理学报,2001,23:81. |
| [22] | 冯尚申,焦正宽.La0.822Sr0.178MnxO3薄膜的输运性质[J].低温物理学报,2001(02):139-143. |
| [23] | 王文虎,王正道,熊玉峰,陈兆甲.反常输运性质Bi2Sr2CaCu2O8单晶的生长[J].低温物理学报,2001(03):184-187. |
| [24] | 戴建明,杨一军,方军,宋文海.多晶Ba2FeMoO6的溶胶-凝胶制备及其结构、磁性和磁电阻效应研究[J].低温物理学报,2002(03):167-172. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%