采用溶胶-凝胶法并经不同温度烧结而制备了名义组分为La2/3Ca1/3MnO3和La2/3Ca1/3Mn1-xCuxO3(x=4%)的系列样品,对它们进行了阻温关系测量.从试验结果观察到:在La2/3Ca1/3MnO3样品中,降温和升温测量的阻温曲线几乎完全重合,没有观察到明显的热弛豫现象.而在不同温度烧结的La2/3Ca1/3Mn1-xCuxO3(x=4%)样品中,阻温关系有明显的热弛豫现象.同时试验还观察到该热弛豫现象随样品烧结温度(颗粒尺寸)的增加逐渐消失.
参考文献
| [1] | Rvon Helmolt;JWecker;BHolzapfel;LSchultz, and KSamwer .[J].Physical Review Letters,1993,71:2331. |
| [2] | S Jin et al.[J].Science,1994,264:413. |
| [3] | A Gupta et al.[J].Physical Review B,1996,54:R15629. |
| [4] | R D Sanchez et al.[J].Applied Physics Letters,1996,68:134. |
| [5] | L E Hueso;JRivas;F Rivadulla;M A Lopez-Quintela .[J].Journal of Applied Physics,1999,86:3881. |
| [6] | H Y Hwang;S-WCheong;P GRadaelli;MMarezio,andBBatlogg .[J].Physical Review Letters,1995,75:914. |
| [7] | G Turilli;F Licci .[J].Physical Review B,1996,54:1305. |
| [8] | K H Ahn;XWWu;K Liu;C L Chien .[J].Physical Review B,1996,54:15299. |
| [9] | K Ghosh;SBOgale;R Ramesh et al.[J].Physical Review B,1999,59:533. |
| [10] | S A Sergeenkov;HBougrine;M Ausloose et al.[J].JETP Letters,1999,69:858. |
| [11] | S L Yuan;ZYLi;G Q Zhang et al.[J].Solid State Communications,2001,117:661. |
| [12] | S L Yuan;JTang;Z C Xia .[J].Journal of Physics D:Applied Physics,2003,36:1446. |
| [13] | R D Sanchez;JRivas;C Vazquez et al.[J].Applied Physics Letters,1996,68:134. |
| [14] | S L Yuan;YPYang;Z C Xia et al.[J].Physical Review B,2002,66:172402. |
| [15] | 李光临,孟立飞,李志强,韩柯,高政祥,张西祥,温戈辉,郑荣坤.熔融织构块材和单晶YBa2Cu3O7在63～75K的磁弛豫性质[J].低温物理学报,2001(03):174-178. |
| [16] | 冯尚申,焦正宽.用溶胶-凝胶法合成La1-xCaxMn1.03O3（x≥0.5）薄膜的电磁性质[J].低温物理学报,2001(03):211-215. |
| [17] | 李光临,宋炜,孟立飞,冯庆荣,高政祥,张西祥,温戈辉,郑荣坤.MgB2超导块材的非线性磁弛豫性质的研究[J].低温物理学报,2001(04):309-312. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%