本文采用直流磁控溅射方法在(100)取向的LaAlO3基片上制备了系列多层膜: La0.67Ca0.33MnO3-δ/La0.67Sr0.33MnO3-δ/La0.67Ca0.33MnO3-δ (LC/LS/LC).并采用标准四探针方法对所制备样品的阻温关系进行了测量. 结果表明:在零场下,当上下两层厚度一定时,随着中间层(LS)厚度增加,多层膜的电阻率减小,金属-绝缘体转变温度(TM-I)向高温方向移动.在中间层(LS)厚度保持一定时,随着上下两层(LC)厚度增加,其电阻率和金属-绝缘体转变温度(TM-I)出现同样的变化规律.基于双交换理论,我们对以上结果给出了尝试性解释.
参考文献
[1] | R von Helmolt;J Wecker;B Holzapfel;L, Schultz, and K.Samwer .[J].Physical Review Letters,1993,71:2331. |
[2] | K Chahara;T Ohno;M Kasai;Y.Koozono .[J].Applied Physics Letters,1993,63:1990. |
[3] | M McCormack;S Jin;T H Tiefel;R.M.Fleming, J.M.Phillips, and R.Ramesh .[J].Applied Physics Letters,1994,64:3045. |
[4] | H L Ju;J Gopalakrishnan;J L Peng;Q.Li, G.C.Xiong, T.Venkatesan, and R.L.Greene .[J].Physical Review,1995,B51:6143. |
[5] | G Q Gong;C Canedy;G Xiao;J.Z.Sun, A.Gipta, and W.J.Gallagher .[J].Applied Physics Letters,1995,67:1783. |
[6] | H Kuwahara;Y Tomioka;A Asamitsu;Y.Moritomo, and Y.Tokura .[J].Science,1995,270:961. |
[7] | Hwang H Y et al.[J].Physical Review Letters,1995,75:914. |
[8] | G Q Gong;A Gupta;Gang Xiao;P.Lecoeur and T.R.McGuire .[J].American Physiological Society,1996,54:3742. |
[9] | Srinivas V;Pietambaram;D Kumar;Rajiv K.Singh, and Clinton B.Lee .[J].Applied Physics Letters,2001,78:243. |
[10] | CaoShui Xiong;YeQing Tang;Jie Gao;Hong Zhu, Li Pi, KeBin Li, JingSheng Zhu, and YuHeng Zhang .[J].Physical Review,1999,B59:9437. |
[11] | G H Jonker;J H Van Santen .[J].Physical A(Amsterdam),1950,16:337. |
[12] | 熊光成,连贵君,康晋峰,孙云锋.异质外延生长钙钛矿结构氧化物薄膜[J].低温物理学报,1999(04):241-246. |
[13] | 连贵君,王永忠,熊光成,高矩,华志强.在SrTiO3、LaAlO3和Y-ZrO2衬底上外延生长La1.85Sr0.15CuO4、La2CuO4和Nd1.85Ce0.15CuO4、Pr2CuO4薄膜[J].低温物理学报,2000(01):1-7. |
[14] | 赵中云,李建青,田旭.Mn基钙钛矿氧化物中的自旋极化隧道输运[J].低温物理学报,2003(02):127-131. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%