我们测量了最佳掺杂的Nd1.85Ce0.15CuO4单晶的电阻率和ab面以及c方向热电势. ρ-T曲线在高温下表现为非常好的直线,超导转变比较尖锐Tc,mid=20.6K,说明我们的样品品质很好.低温下的电阻率拟合结果表明频率大约100K的软声子模与载流子有强烈相互作用,这是极化子模型有力的证据.对于热电势结果,令人惊奇的是,无论数值还是曲线形状,包括低温曳引峰的位置,c方向的热电势Sc与ab面内的热电势Sab非常接近.这可能是某种共同的机制导致的结果.比较Nd1.85Ce0.15CuO4和Sm1.85Ce0.15CuO4的热电势曲线可以发现,二者的数值和曲线形状基本相同,而与La1.85Sr0.15CuO4差异较大,这进一步说明了顶点氧在这些体系中的作用.
参考文献
| [1] | Y Tokura;H Takagi;S Uchida .[J].Nature,1989,337:345. |
| [2] | H Takagi;S Uchida;Y Tokura .[J].Physical Review Letters,1989,62:1197. |
| [3] | Suzuki;K Kishio;T Hasegawa .[J].PHYSICA C,1990,166:357. |
| [4] | S Uchida;T Ido;H Takagi;T Arima,Y Tokura,and S Tajima .[J].Physical Review B,1991,43:7942. |
| [5] | S L Cooper;G A Thomas;A J Millis;J Orenstein,D H Rapkine,A J Millis,S-W Cheong,A S Cooper,and Z Fisk .[J].Physical Review B,1990,41:11605. |
| [6] | D H Wu;J Mao;S N Mao;J L Peng,X X Xi,T Venkatesan,R L Greene,and S M Anlage .[J].Physical Review Letters,1993,70:85. |
| [7] | B Stadlober;G Krug;R Nemeschek;R Hackl,J L Cobb,and J T Markert .[J].Physical Review Letters,1995,74:4911. |
| [8] | A Urushibara et al.[J].Physical Review B,1995,51:14103. |
| [9] | Jaime et al.[J].Physical Review B,1998,58:R5901. |
| [10] | Guo-meng Zhao;V Smolyaninova;W Prellier;H Keller .[J].Physical Review Letters,2000,84:6086. |
| [11] | I G Land;Yu A Firsov .[J].Soviet Physics JETP,1963(16):1301. |
| [12] | G H Chen et al.[J].MODERN PHYSICS LETTERS B,1989,4(04):295. |
| [13] | 柴一晟,杨宏顺,刘剑,余旻,曹烈兆.Sm2-xCexCuO4单晶的赝能隙行为研究[J].低温物理学报,2004(01):26-30. |
| [14] | 柴一晟,杨宏顺,刘剑,纪明,曹烈兆.电子型超导体Sm1.85Ce0.15CuO4单晶样品的制备和品质鉴定[J].低温物理学报,2003(01):30-34. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%