采用叔胺化反应与季铵化反应2步高分子反应过程,制备季铵化的聚乙烯亚胺(QPEI),采用静态挂片失重法与电化学极化曲线测定法,研究了在H2S04溶液中QPEI对低碳钢的缓蚀性能与缓蚀机理,并使用扫描电子显微镜对缓蚀样片表面膜层进行了分析. 实验结果表明,QPEI对低碳钢具有优良的缓蚀作用,在0.5 mol/L的H2S04介质中,QPEI的质量浓度仅为5 mg/L,A3钢片的腐蚀时间为72 h时,缓蚀率高达91%;QPEI可同时抑制阴极过程与阳极过程,其缓蚀作用属混合型;在物理吸附与化学吸附的协同下,QPEI在碳钢表面会形成致密的吸附膜,它在钢板表面的吸附行为符合Langmuir单分子层吸附等温式.
参考文献
[1] | Qiu L G,Xie A J,Shen Y H.Mater Chem Phys[J],2005,91:269 |
[2] | Ramesh S,Rajeswari S.Electrochim Acta[J],2004,49:811 |
[3] | Ashassi-Sorkhabi H,Shabani B,Aligholipour B,Seifzadeh D.Appl Surf Sci[J],2006,252:4 039 |
[4] | Bentiss F,Gassama F,Barbry D,Gengembre L,Vezin H,Lagrenée M,Traisnel M.Appl Surf Sci[J],2006,252:2 684 |
[5] | Bouklah M,Hammouti B,Aouniti A,Benhadda T.Prog Org Coat[J],2004,49:225 |
[6] | Wang H L,Fan H B,Zheng J S.Mater Chem Phys[J],2002,77:655 |
[7] | Abed Y,Kissi M,Hammouti B,Taleb M,Kertit S.Prog Org Coat[J],2004,50:144 |
[8] | Gunasekaran G,Chauhan L R.Electrochim Acta[J],2004,49:4 387 |
[9] | Jianguo Y,Lin W,Otieno-Alego V,Schweinsberg D P.Corros Sci[J],1995,37:975 |
[10] | Migahed M A,Aly R O,Al-Sabagh A M.Corros Sci[J],2004,46:2 503 |
[11] | Yfantis A,Paloumpa I,Schmei D,Yfantis D.Surf Coat Technol[J],2002,151-152:400 |
[12] | Ali S A,Saeed M T.Polymer[J],2001,42:2 785 |
[13] | GAO Shui-Ying(高水英),YU Lai-Gui(余来贵).Acta Polym Sin(高分子学报)[J],2003,(1):18 |
[14] | Hwang S,Lee K T,Park J W,Min B-R,Haam S,Ahn I-S,Jung J-K.Biochem Eng J[J],2004,17:85 |
[15] | Bisset W,Jacobs H,Koshti N.React Funct Polym[J],2003,55:109 |
[16] | Reybier K,Zairi S,Jaffrezic-Renault N.Talanta[J],2002,56:1 015 |
[17] | Rosa G D,Bochot A,Quaglia F.Int J Pharm[J],2003,254:89 |
[18] | HUANG Jin-Ying(黄金营),ZHENG Jia-Shen(郑家燊),WEI Hong-Biao(魏红飚).Corros Sci Protect Technol(腐蚀科学与防护技术)[J],2004,16(5):272 |
[19] | Ita B I,Offiong O E.Mater Chem Phys[J],2001,70:330 |
[20] | ZHANG Xin(张昕),GAO Bao-Jiao(高保娇),WANG Rui-Xin(王蕊欣),LI Gang(李刚).Chinese Syn Chem(合成化学)[J],2007,15(3)(已录用) |
[21] | LI Zheng-Hui(李正惠),FU Li(傅莉).Beijing Chem Eng Univ(北京化工大学学报)[J],1999,26(3):61 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%