研究了由H2S气体,(CoS-Mo2S) /BaCe0.475Zr0.475Y0.05O3-δ/Ag,空气构成的质子传导型固体氧化物燃料电池的制备和电性能,以及在常压、温度范围为600～800 ℃时,温度和燃料气流量对H2S脱除率的影响. 结果表明,H2S脱除率与电流密度之间呈线性关系;电池电流密度和H2S脱除率均随温度的升高而增大,电池适宜工作温度范围为700～800 ℃;在30～80 mL/min范围内,H2S脱除率随燃料气流量增加而增大;在反应温度为800 ℃、燃料气流量为80 mL/min的条件下,电池开路电压为0.72 V,最大电流密度为2.9×10-2 A/cm2,H2S脱除率可达71%.
参考文献
| [1] | Pujare N U,Semkow K W,Sammells A F.J Electrochem Soc[J],1987,134(10):2 639 |
| [2] | Aguilar L,Zha S W,Cheng Z,Winnick J,Liu M L.J Power Sources[J],2004,135:17 |
| [3] | Liu M,He P,Luo J L,Sanger A R,Chuang K T.J Power Sources[J],2001,94:20 |
| [4] | Peterson D,Winnick J.J Electrochem Soc[J],1998,145(5):1 449 |
| [5] | TAN Wen-Yi(谭文轶),ZHONG Qin(钟秦).J Chinese Ceram Soc(硅酸盐学报)[J],2006,34(8):970 |
| [6] | Chuang K T,Donini J C,Sanger A R,Slavov S V.Int J Hydrogen Energy[J],2000,25:887 |
| [7] | Chuang K T,Sanger A R,Slavov S V,Donini J C.Int J Hydrogen Energy[J],2001,26:103 |
| [8] | ZHONG Li(钟理),CHEN Jian-Jun(陈建军),Wei G L,Luo J L,Chuang K T.J Chem Ind Eng(化工学报)[J],2004,55(10):1 732 |
| [9] | Ringuede′ A,Labrincha J A,Frade J R.Solid State Ionics[J],2001,141-142:549 |
| [10] | Mather G C,Figueiredo F M,Jurado J R,Frade J R.Solid State Ionics[J],2003,162～163:115 |
| [11] | TAN Wen-Yi(谭文轶),ZHONG Qin(钟秦),FENG Feng(冯凤).Chinese J Nonfer Met(中国有色金属学报)[J],2006,16(6):1 052 |
| [12] | BAO Jun(鲍骏),BIAN Guo-Zhu(卞国柱),FU Yi-Lu(伏义路).Chinese J Catal(催化学报)[J],1999,20 (6):645 |
| [13] | Harvey S,Davidson J H,Fletcher E A.Ind Eng Chem Res[J],1998,37:2 323 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%