研究了Ti0.8Zr0.2V1.1Mn0.9-xNi0.4Crx(x为0～0.4)固溶体电极合金的结构和电化学性能. 结果表明,Ti0.8Zr0.2V1.1Mn0.9-xNi0.4Crx系列合金是由具有体心立方(BCC)结构的V基固溶体相和C14 Laves第二相组成的双相合金. Ti0.8Zr0.2V1.1Mn0.9-xNi0.4Crx系列合金作为镍-氢化物电池负极材料具有良好的活化性能(3次循环可以达到最大放电容量)和倍率放电能力;由于Cr取代Mn抑制了合金中吸氢元素V充放电过程中在电解液中溶解,显著改善了此系列合金电极的循环寿命,20周循环后循环稳定性系数S20从6.4%(x=0)增加到73.8%(x=0.4);合金电极的最大放电容量随Cr取代量的增加从420 mA·h/g(x=0)降低到279 mA·h/g(x=0.4);高温放电容量随着Cr取代量的增加而降低,333 K温度条件下,放电容量从744 mA·h/g(x=0)减少到246 mA·h/g(x=0.4);Ti0.8Zr0.2V1.1Mn0.9-xNi0.4Crx系列合金电极的交换电流密度和氢扩散系数均随Cr取代量增加而先增大后减小,当x=0.3时最大,分别为275 mA/g和5.956×10-10 cm2/s.
参考文献
| [1] | Pan H G,Zhu Y F,Gao M X,Wang Q D.J Electrochem Soc[J],2002,149:829 |
| [2] | Chen J,Kuriyama N,Takeshita H T,Tanaka H,Sakai T,Haruta M.Electrochem Solid-State Lett[J],2000,3(6):249 |
| [3] | Iba H,Akiba E.J Alloys Compd[J],1995,231:508 |
| [4] | Akiba E,Iba H.Intermetallics[J],1998,6:461 |
| [5] | Akiba E,Enoki H.Materia Japan[J],1998,37:645,in Japanese |
| [6] | Huot J,Akiba E,Iba H.J Alloys Compd[J],1995,228:181 |
| [7] | Iba H,Mouri T,Shionoya M,Akiba E.Materia Japan[J],1997,36:640,in Japanese |
| [8] | QIAO Yu-Qing(乔玉卿),ZHAO Min-Shou(赵敏寿),LI Mei-Ye(李梅晔),ZHU Xin-Jian(朱新坚),CAO Guang-Yi(曹广益).Chinese Inorg Chem(无机化学学报)[J],2006,22:415 |
| [9] | Yin W Y,Zhao M S.Electrochim Acta[J],2007,52(7):2 723 |
| [10] | Pan H G,Li R,Gao M X,Liu Y F,Wang Q D.J Alloys Compd[J],2005,(404-406):669 |
| [11] | Kim J H,Lee H,Lee P S,Seo C Y,Lee J Y.J Alloys Compd[J],2003,348:293 |
| [12] | Beeri O,Cohen D,Gavra Z,Mintz M H.J Alloys Compd[J],2003,352:111 |
| [13] | Tamura T,Tominaga Y,Matsumoto K,Fuda T,Kuriiwa T,Kamegawa A,Takamura H,Okada M.J Alloys Compd[J],2002,(330-332):522. |
| [14] | Ovshinsky S R,Fetcenko M A.J Ross Sci[J],1993,260:176 |
| [15] | Sakai T,Miyamura H,Kuriyama N,Kato A,Ources K,Inshikawa H.J Less-Commen Met[J],1990,159:127 |
| [16] | Kuriyama N,Sakai T,Miyamura H,Uehara I,Ishikawa H,Iwasaki T.J Electrochem Soc[J],1992,139:172 |
| [17] | Kuriyama N,Sakai T,Miyamura H,Uehara I,Ishikawa H.J Alloys Compd[J],1993,202:183 |
| [18] | Zheng G,Popov B N,White R E.J Electrochem Soc[J],1995,142:2 695 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%