合成了离子液体[bmim]PF6,通过其与MMA的在位聚合用作PMMA的增塑剂,用DSC和TG等方法测定了增塑前后聚合物的玻璃化转变温度和热稳定性.结果表明,当离子液体[bmim]PF6的体积分数从0增至到60%时,聚合物的玻璃化转变温度(Tg)由105 ℃降至室温(20 ℃)以下,且几乎呈线性下降趋势,相应的热质量损失从4.19%降至0.16%,说明离子液体能够显著地降低PMMA的Tg,提高塑料的热稳定性能.
参考文献
| [1] | Rogers R D,Seddon K R.Science[J],2003,302:792 |
| [2] | Seddon K R.Nature Mater[J],2003,2:363 |
| [3] | CHEN Hui(陈慧),DAI Li-Yi(戴立益),SHAN Yong-Kui(单永奎),et al.Chinese J Appl Chem(应用化学)[J],2003,20(9):829 |
| [4] | ZHANG Pu-Yu(张普玉),LOU Shuai(娄帅),CHAI Yun(柴云).Petrochem Tech(石油化工)[J],2005,34(4):388 |
| [5] | Wei G T,Yang Z,Chen C J.Anal Chim Acta[J],2003,488:183 |
| [6] | Zhang S,Zhang Q,Zhang Z C.Indust Eng Chem Res[J],2004,43:614 |
| [7] | Weyershausen B,Lehmann K.Green Chem[J],2005,7:16 |
| [8] | National Toxicology Programme.DHHS Publ No(NIH) 82-1773,1982 |
| [9] | Schmidt F G,Petrat F M,Pawlik A,et al.WO 04 005 391[P],2004 |
| [10] | Rahman M,Brazel C S.Polym Prepr(Am Chem Soc),2004,45,1:301 |
| [11] | Carda-Broch S,Berthod A,Armstrong D W.Anal Bioanal Chem[J],2003,375:193 |
| [12] | WANG Hai-Zhong(王海忠),YE Cheng-Feng(叶承峰),LIU Wei-Min(刘维民).Tribology(摩擦学学报)[J],2003,23(1):38 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%