以快速溶胶法制备了纳米TiO2光催化剂,用于室温下固相光催化降解聚乙烯(PE)包装薄膜的研究. 对催化剂和薄膜进行了X射线衍射分析,傅立叶红外光谱分析,扫描电子显微镜形貌观察. 结果表明,15 W紫外光辐射240 h后,PE质量损失为7.66%,金红石型纳米TiO2光催化剂使PE质量损失14.93%,锐钛矿型纳米TiO2光催化剂使PE质量损失23.97%;TiO2加速了高分子碳链的断裂和光氧化,在薄膜表面形成大量的凹坑,降解产物中小分子量的石蜡含量明显增高,锐钛矿型纳米TiO2光催化降解PE的活性高于金红石型纳米TiO2.
参考文献
| [1] | Gugumus F. Polym Degrad Stab[J],1999,16:161 |
| [2] | Fujishima A,Tata N Rao,Donald A, et al. J Photochem Photobiol C:Photochem Rev[J],2000,1:1 |
| [3] | Anpo M,Takeuchi M, T J. Catalysis[J],2003,216:505 |
| [4] | Shang J,Chai M,Zhu Y. J Solid State Chem[J],2003,174:104 |
| [5] | Shang J,Chai M,Zhu Y. Environ Sci Techn[J],2003,37:4 494 |
| [6] | Ajit S. Radiation Phy Chem[J],1999,56:375 |
| [7] | Gugumus F. Polym Degrad Stab[J],2002,76:329 |
| [8] | Gugumus F. Polym Degrad Stab[J],1998,62:235 |
| [9] | YU Jiu-Gao(于九皋),HUANG Xiao-Dong(黄晓东). Chin J Appl Chem(应用化学)[J],2001,18(1):48 |
| [10] | Hlangothi S P,Krupa I,Djokovic V, et al. Polym Degrad Stab[J],2003,79:53 |
| [11] | Seong O H,Dong W L,Oc H H. Polym Degrad Stab[J],1999,63:237 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%