采用电沉积技术制备羟基磷灰石(HA)/TiO2复合涂层,比较了不同工艺条件对涂层中TiO2含量的影响,测试了涂层的结合强度,探讨了结合强度和TiO2含量的关系,实验结果表明,涂层中TiO2的含量随电流密度的降低、电沉积时间的延长和电解液中TiO2浓度的提高而增加,随主盐浓度的升高先增加后减小.结合强度随涂层中TiO2含量的增加而提高,经烧结后涂层的结合强度显著提高,涂层中TiO2质量分数为72.2%时,其结合强度可达18.7 MPa.复合涂层的耐腐蚀性较好,具有良好的化学稳定性和抗溶解性.当烧结温度高于800℃时,TiO2起催化作用促进HA分解,产生新相β-Ca3(PO4)2和CaO.
参考文献
| [1] | Gricia R,Dorcmus R H. J Mater Sci:Mater Med[J] ,1992,3:154 |
| [2] | Lo W J,Grant D M. J Biomed Mater Res[J] ,2000,50(4) :536 |
| [3] | Pham M T. J Mater Sci Lett[J] ,2000,19(5) :443 |
| [4] | Clies L. J Biomed Mater Res[J] ,2000,49(1) :43 |
| [5] | Shirkhanzadeh M. J Mater Sci Lett[J] ,1991,10:1 415 |
| [6] | Zhitomirsky I. J Mater Sci:Mater Med[J] ,1997,8:213 |
| [7] | ZHENG Xue-Bin(郑学斌),ZHOU Xia-Ming(周霞明),ZHANG Ye-Fang(张叶方),et al.J Inorg Mater(无机材料学报)[J],1999,14(6):956 |
| [8] | Lia H,Khora K A,Cheangb P. Biomaterials[J] ,2002,23:85 |
| [9] | Milella E,Cosentino F,Licciulli A, et al. Biomaterials[J] ,2001,22:1 425 |
| [10] | Roop Kumar R,Wang M. Mater Lett[J] ,2002,55:133 |
| [11] | Nie X,Leyland A,Matthews A. Surface Coat Tech[J] ,2000,125:407 |
| [12] | Shirkhanzadeh M. J Mater Sci:Mater Med[ J] ,1998,9:67 |
| [13] | Han Y,Fu T,Lu J, et al. J Biomed Mater Res[J] ,2001,54:96 |
| [14] | LIU Rong-Fang(刘榕芳),XIAO Xiu-Feng(肖秀峰),ZHENG Li-Qun(郑立群),et al.Chin J Appl Chem(应用化学)[J],2003,20(6):547 |
| [15] | Ban S,Maruno S. J Biomed Mater Res[J] ,1998,42:387 |
| [16] | ChemJ H,Liu M L. JMaterSci:MaterMed[J] ,1994,5:279 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%