用DSC和WAXD研究了聚丙烯-g-聚氨酯(PP-g-PU)共聚物的组成对其结晶行为的影响. 结果表明,由于PU支链的存在,PP-g-PU的结晶熔融峰要比纯PP的低,而结晶温度则有所提高;PP-g-PU的结晶总速率随其PU含量增加而增大;PP接枝PU后,结晶行为发生了变化, 微晶尺寸明显增大. 不同晶面的增长也因PU支链含量的不同而存在差异;PP-g-PU的结晶度随PU含量的增加呈现先增后减的趋势.
参考文献
| [1] | Mehta J K,Sood D S,Mishra B N. J Polym Sci:Polym Chem Ed[J],1989,27:53 |
| [2] | Tazulce S,Kimura H. Makromol Chem[J],1978,179:2 603 |
| [3] | Manson J A,Sperling L H. Polymer Blends and Composites[M]. Chapts2 and 13. New York:Plenum Press,1976 |
| [4] | Fujiyama M,Wakino T. J Appl Polym Sci[J],1991,42:9 |
| [5] | Fujiyama M,Wakino T. J Apple Polym Sci[J],1991,42:2 739 |
| [6] | LIU Ye-Qiu(刘冶球). Doctoral Dissertation([博士学位论文]). Guangzhou(广州):Zhongshan University(中山大学),2001 |
| [7] | Gupta A K,Gupta V B,Peters R H, et al. J Appl Polym Sci[J],1982,27:4 669 |
| [8] | Beck H N,Ledbetter H D. J Appl Polym Sci[J],1965,9:2 131 |
| [9] | Seo Y,Kim J,Kim K U, et al. Polymer[J],2000,41:2 639 |
| [10] | Weidinger A,Herkmans P H. Makromol Chem[J],1961,50:98 |
| [11] | PAN Yong-Kang(潘泳康),YUAN Ji-Min(阮吉敏),ZHOU Da-Fei(周达飞). Polym Mat Sci Eng(高分子材料科学与工程)[J],1999,3:159 |
| [12] | George S,Varughese K T,Thomas S. Polymer[J],2000,41:5 485 |
| [13] | YANG Jun(杨军),LIU Wan-Jun(刘万军),CHEN Guang-Xin(陈广新), et al. Acta Polym Sinica(高分子学报)[J],2001,3:383 |
| [14] | Alexander L E. X-ray Diffraction Methods in Polymer Science[M]. New York:Wiley,1969:423 |
| [15] | YU Xiao-Qiang(于晓强),WANG Jing-Yuan(王静媛),LI Feng(李峰), et al. Acta Polym Sinica(高分子学报)[J],1998,1:26 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%