采用真空电弧熔炼法和高温淬火法制备了四元哈斯勒合金Ni5o-xCuxMn36Sn14(x=0,2,4,6)的化合物.用X射线衍射仪和振动样品磁强计研究了合金的物相与磁热效应.结果表明,部分Cu元素对Ni的替代,并没有改变三元哈斯勒合金Ni-Mn-Sn原有的晶体结构,只是晶格常数开始有减小的趋势,晶胞的体积没有发生太大的变化.M-T曲线的结果表明,该系列哈斯勒合金样品在奥氏体相的铁磁交换作用增强,导致居里温度升高,而结构相变温度降低.此外,通过麦克斯韦方程计算了该系列合金的磁熵变(-△Sm),在磁场变化为1.5T的情况下,获得了Ni46Cu4 Mn36Sn14合金在330 K附近的最大磁熵变(-△Smaxm)约为2.0 J·(kg·K)-1.
参考文献
| [1] | Gao, B;Shen, J;Hu, FX;Wang, J;Sun, JR;Shen, BG .Magnetic properties and magnetic entropy change in Heusler alloys Ni50Mn35-x Cu (x) Sn-15[J].Applied physics, A. Materials science & processing,2009(2):443-447. |
| [2] | Hu F X;Wang J;Shen J;Gao B Sun J R Shen B G .Large magnetic entropy change with small therml hysteresis near room temperature in metamagnetic alloys Ni51 Mn49-xInx[J].Journal of Applied Physics,2009,105:07A940. |
| [3] | L. Pareti;M. Solzi;F. Albertini;A. Paoluzi .Giant entropy change at the co-occurrence of structural and magnetic transitions in the Ni_(2.19)Mn_(0.81)Ga Heusler alloy[J].The European physical journal, B. Condensed matter physics,2003(3):303-307. |
| [4] | 张浩雷,李哲,乔燕飞,曹世勋,张金仓,敬超.哈斯勒合金Ni-Co-Mn-Sn的马氏体相变及其磁热效应研究[J].物理学报,2009(11):7857-7863. |
| [5] | 柳祝红,胡凤霞,王文洪,陈京兰,吴光恒,高书侠,敖玲.哈斯勒合金Ni-Mn-Ga的马氏体相变和磁增强双向形状记忆效应[J].物理学报,2001(02):233-238. |
| [6] | 敬超,李哲,陈继萍,鲁玉明,曹世勋,张金仓.哈斯勒合金Ni-Mn-Sn的马氏体相变与反磁热性质[J].物理学报,2008(06):3780-3785. |
| [7] | Thorsten Krenke;Eyüp Duman;Mehmet Acet;Eberhard F Wassermann Xavier Moya Lluis Ma(n)osa Antoni Planes .Inverse magnetocaloric effect in ferromagnetic Ni-Mn-Sn alloys[J].Applied Physics,2004,34:1097. |
| [8] | 朱志永,王文全,苗元华,王岩松,陈丽婕,代学芳,刘国栋,陈京兰,吴光恒.掺杂对Ni51.5 Mn25 Ga23.5相变行为和磁性的影响[J].物理学报,2005(10):4894-4897. |
| [9] | 韩志达,崔荣静,江学范,王敦辉,都有为.Ni_（43）Mn_（46-x）T_xSn_（11）（T=Fe,Co,Ni）合金的马氏体相变和磁熵变[J].稀有金属,2010(01):115-120. |
| [10] | 李哲,敬超,乔燕飞,张浩雷,曹世勋,张金仓,孙亮.哈斯勒合金Ni46Cu4Mn38Sn12的相变应变与磁感生应变[J].中国有色金属学报,2010(11):2187-2191. |
| [11] | 王大伟,林志平,李山东,黄志高,都有为.Ni45.4+x Mn41.5-xSn13.1（x=0,1.5,3.0）合金的结构和磁熵变研究[J].金属功能材料,2009(02):1-4. |
| [12] | Feng, WJ;Zhang, Q;Zhang, LQ;Li, B;Du, J;Deng, YF;Zhang, ZD .Large reversible high-temperature magnetocaloric effect in Ni50-xMn38+xSb12 alloys[J].Solid State Communications,2010(19/20):949-952. |
| [13] | 柳祝红,吴光恒,王文洪,陈京兰,敖玲,金重勋.内应力对铁磁性形状记忆合金Ni-Mn-Ga马氏体相变路径的影响[J].物理学报,2002(03):640-644. |
| [14] | 敖玲;王文洪;陈京兰;高淑侠 吴光恒 .哈斯勒合金Ni-Mn-Ga中间马氏体相变研究[J].物理学报,2002,50(04):793. |
| [15] | 李健靓,赵韦人,张羊换,王新林,张建福,郭世海.熔体快淬对Ni-Mn-Ga合金马氏体相变特征及应变的影响[J].物理学报,2003(11):2849-2853. |
| [16] | 耿遥祥,特古斯,毕力格,王伟,哈斯朝鲁,松林.热处理工艺对（ Mn,Fe）2（P,Si）系列化合物磁性的影响[J].稀有金属,2011(06):871-876. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%