添加少量Zr能增大LaNi3.8Al0.75Mn0.45合金氢化反应的焓变, 从而降低其室温的吸氢平台压力, 但吸氢量变化不显著, 合金表现出了与LaNi3.8Al0.75Mn0.45合金相当的贮氢性能.而Zr元素的添加使得LaNi3.8Al0.75Mn0.45Zr0.05合金中形成了多种非吸氢的杂质相, 同时由于Zr固溶到基体中提高了基体的强度, 合金的抗粉化性能得到了很大的提高.
参考文献
[1] | 大角泰章.金属氢化物的性质与应用[M].北京:化学工业出版社,1990 |
[2] | Joubert J M;Cerny R;Latroche M;Percheron-Guégan A Yvon K .Compressibility and thermal expansion of LaNi5 and its substitutional derivatives (LaNi5-xMx;M=Mn,Al,Co)[J].Intermetallics,2005,13:227. |
[3] | Nakamura H;Nakamura Y;Fujitani S;Yonezu I .A method for designing a hydrogen absorbing LaNi5-x-yMnxAly alloy for a chemical refrigeration system[J].Journal of Alloys and Compounds,1997,252:83. |
[4] | 张瑞静,吕曼祺,陈德敏,杨柯.LaNi5-xMx(M=Al,Mn)合金的稳定性及储氢性能研究[J].金属学报,2005(04):427-432. |
[5] | 蒋于伟,刘晓鹏,蒋利军,王树茂,杨洪广.LaNi4Al0.75M0.25(M=Mn,Sn,In,Ti,Zr)合金吸放氢性能研究[J].稀有金属,2007(04):407-411. |
[6] | Osumi Y;Suzuki H;Kato A;Oguro K,Kawai S,Kaneko M .Hydrogen absorption-desorption characteristics of Mm-Ni-Al-M and Mm-Ni-Mn-M alloys (Mm misch metal)[J].Journal of the Less-Common Metals,1983,89:287. |