用Si,Mo和Nb作为起始原料通过预烧结、氮化反应和N2气氛下的热压烧结制备出Si3N4/MoSi2/NbN复合材料,借助扫描电镜和X射线衍射等分析手段对各阶段样品的相组成和显微组织进行了表征,结果表明:在预烧结阶段获得了NbN, MoSi2和未反应的Si相;随着温度的提高,氮化反应生成了α-Si3N4和少量β-Si3N4;最后经热压烧结制备了Si3N4/MoSi2/NbN复合材料.
参考文献
[1] | Wang CM.;Ruhle M.;Riley FL.;Mitomo M.;Pan XQ. .SILICON NITRIDE CRYSTAL STRUCTURE AND OBSERVATIONS OF LATTICE DEFECTS [Review][J].Journal of Materials Science,1996(20):5281-5298. |
[2] | 汪东亮.精细陶瓷材料[M].北京:中国物资出版社,2000:87. |
[3] | 刘渝珍.Si3N4-TiN的氧化行为和显微结构的研究[J].电子显微学报,1990(03):167. |
[4] | 张炳荣,沈建兴.Si3N4/MoSi2陶瓷的制备工艺与组织研究[J].机械工程材料,2000(05):8-10. |
[5] | 邹红,邹从沛.TiN颗粒增韧Si3N4复合材料氧化行为的研究[J].核动力工程,2002(04):1-4,11. |
[6] | Yu Kelina;Plyasunkova L A;Chevykalova L A .High-temperature oxidation resistance of ceramic matrix composites Si3N4-Cf[J].Powder Metallurgy and Metal ceramics,2003,42(06):592. |
[7] | Petrovic John J;Pena Maria I .Frication and microstructures of MoSi2 peinforced-Si3N4 matrix composites[J].Journal of the American Ceramic Society,1997,80(05):1111. |
[8] | Tampieri A;Bellosiand A;Biasini V.Oxidation resistance of Si3N4-TiB2 composites[J].See REF,1998(06):409. |
[9] | Zhang S;Munir Z A.The combustion synthesis of refractory nitrides[J].Journal of Materials Science,1991(26):3380. |
[10] | Agrafiotis C C;Puszynski J A;Hlavacek V .Effect of metal particle morphology on the combustion of refractory metals in nitrogen[J].Journal of the American Ceramic Society,1991,74(11):2912. |
[11] | 颜建辉,张厚安,李益民.不同致密度MoSi2材料在700~1200 ℃的氧化行为[J].稀有金属,2007(01):18-21. |
[12] | 颜建辉,张厚安,唐思文,李益民.La2O3-Mo5Si3/MoSi2复合材料的高温氧化行为[J].中国稀土学报,2006(05):551-555. |
[13] | 卡恩 R W;哈森 P;克雷默 E J.陶瓷结构与性能[M].北京:科学出版社,1998:107. |
[14] | 张永刚;韩雅芳;郭建亭;万晓景 冯涤.金属间化合物结构材料[M].北京:国防工业出版社,2001:870. |
[15] | Ordonez S. .The influence of amount and type of additives on α→β Si3N4 transformation[J].Journal of Materials Science,1999(1):147-153. |
[16] | Honma T;Ukyo Y.Sintering process of Si3N4 with Y2O3 and Al2O3 as sintering additives[J].Journal of Materials Science,1999(18):735. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%