中等Nb含量的、含有O相的Ti3Al基合金以及高Nb含量的O相基合金具有比重小、强度高等特性,是适合于650～700℃使用的高温结构材料.本文介绍了一种中等Nb含量的(α2+O+B2)三相Ti3Al基合金(TD3合金)的热机械处理工艺和微观组织特征,以及典型组织的力学性能,并与一些典型的O相基合金,高温钛合金,高温合金进行了对比.对比结果表明,通过适当的热机械处理进行微观组织控制,TD3合金可以获得与Ti2AlNb基合金相当的比强度和高温蠕变性能,其高温冲击韧性、断裂韧性和低周疲劳性能达到了一些钛合金和高温合金在服役条件下的水平.
参考文献
| [1] | Banerjee D;Gogia A K;Nandy T K et al.A new phase in Ti3Al based alloy with high content of niobium[J].Acta Metallurgica Et Materialia,1988,36(04):871. |
| [2] | Blackburn M J;Smith M P .Improved toughness alloys based on titanium aluminides[R].Report WTDC-TR-89-4095,1985. |
| [3] | Rowe R G .Tri-titanium aluminide alloys containing at least eighteen atom percent niobium[P].US 5032357,1991. |
| [4] | Carisey T E et al.Titanium-based intermetallic alloys[P].US 6132526,2000. |
| [5] | Germann L;Banerjee D;Guedou J Y.Microstructure-property relationships in newly developed multiphase Ti2AlNb-based titanium aluminides[A].Hamburg,Germany,2004:2137. |
| [6] | Thomas M;Marty M .Titanium aluminide which can be used at high temperature[P].US 6176949,2001. |
| [7] | Yang S J;Nam S W;Hagiwara M.The role of W in orthorhombic Ti2AlNbbased intermetallic alloy for the enhancement of creep properties above 700 ℃[A].Hamburg,Germany,2004:2161. |
| [8] | Banerjee D;Baligidad R G;Gogia A K.Engineering multiphase intermetallics[A].Warrendale,PA,USA,2001:43. |
| [9] | 曹京霞;孙育峰;曹春晓 等.Ti3Al-Nb-Mo-(Si)合金的显微组织与力学性能[J].稀有金属,1997,21(01):490. |
| [10] | Cao Jingxia;Bai Fang;Li Zhenxi .High temperature low cycle fatigue behavior of titanium aluminide Ti-24Al-15Nb-1Mo alloy[J].Materials Science and Engineering A-STRUCTURAL MATER,2006,424:47. |
| [11] | 曹春晓;高扬 等.钛-铝系金属间化合物基合金均匀化熔铸工艺[P].CN 93116677.2,1993. |
| [12] | 李世琼;张建伟;程云君.Ti3Al和Ti2AlNb基金属间化合物结构材料研发现状[J].稀有金属材料与工程,2005(zk):104. |
| [13] | 中国航空材料手册[M].北京:中国标准出版社,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%