报道了以钨酸钠、硫酸钴和二亚硝酸二胺铂为主盐、以柠檬酸盐为络合剂电沉积钴铂钨合金的工艺过程. 研究了镀液中钨盐浓度、络合剂浓度、电流密度、镀液温度等沉积条件对钴铂钨合金成份的影响. 结果表明, 在实验条件下, 镀液中钨盐含量的增加、电流密度的增大和镀液温度的升高都会引起合金镀层中的钨含量增大. 络合剂用量的增加使合金镀层中的钨含量下降, 而使钴和铂的含量增加.
参考文献
| [1] | Naoe M;Kazama H;Hoshi Y et al.Properties of amorphous Co-Ta and Co-W films deposited by rf sputtering[J].Journal of Applied Physics,1982,53(01):7846. |
| [2] | Adomon U;Dariel M P;Grunbaum E .Microstructrue of electrodeposited Co-W thin film[J].Journal of Applied Physics,1986,59(06):2002. |
| [3] | Adomon U;Dariel M P;Grunbaum E et al.Irreversible magnetization reversal in some Co-based alloy thin films[J].Journal of Applied Physics,1989,66(01):316. |
| [4] | Wulfhekel W.;Zavaliche F.;Sander D.;Kirschner J.;Gutjahr-Loser T. .Relation between structure, stress, and magnetism in Co/W(001) - art. no. 144422[J].Physical Review.B.Condensed Matter,2001(14):4422-0. |
| [5] | 葛洪良,崔玉建,黄丽红,蒋丽珍,江影.钴钨含量对CoPtW永久磁性薄膜结构及磁性能的影响[C].第十一届全国磁学和磁性材料会议论文集,2002:168-169. |
| [6] | 黄丽红,葛洪良,崔玉建.镀液组成和工艺条件对电沉积钴钨合金成分的影响[J].表面技术,2003(02):41-43. |
| [7] | 葛洪良,崔玉建,黄丽红,蒋丽珍,江影.铂钨含量对CoPtW永久磁性薄膜结构及磁性能的影响[J].稀有金属,2003(05):555-557. |
| [8] | 屠振密.电镀合金原理与工艺[M].北京:国防工业出版社,1993:64. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%