研究了焦耳退火和等温退火对Fe73.5Cu1Nb3Si13.5B9非晶丝巨应力阻抗效应的影响. 实验结果表明, 非晶合金丝经电流密度为 26 A*mm-2的焦耳处理后, 其阻抗最大变化率达到25%, 灵敏度为1.71%*MPa-1; 淬态样品在580 ℃等温退火0.5 h后, 其阻抗最大变化率达到67%, 灵敏度为0.85%*MPa-1. 这两种退火方法都可以明显改善Fe73.5Cu1Nb3Si13.5B9非晶合金丝的巨应力阻抗效应, 阻抗的最大变化率与退火过程中晶化导致的平均各向异性的改变有关, 而灵敏度的差异是由退火方法导致材料机械性能的差异带来的.
参考文献
| [1] | Shen L.P.;Uchiyama T. .Sensitive stress-impedance micro sensor using amorphous magnetostrictive wire[J].IEEE Transactions on Magnetics,1997(5):3355-3357. |
| [2] | Shen L.P.;Naruse Y. .Sensitive stress sensor using amorphous magnetostrictive wires on both ends fixed double beam and diaphragm[J].IEEE Transactions on Magnetics,1999(5):3619-3621. |
| [3] | Kusumoto D.;Shen L.P. .Detection of finger-tip blood vessel pulsation using CoSiB thin amorphous wire CMOS-IC SI sensor[J].IEEE Transactions on Magnetics,1999(5):4115-4117. |
| [4] | Alben R;Becker J J .[J].Journal of Applied Physics,1978,49(03):1653. |
| [5] | Herzer G. .Grain size dependence of coercivity and permeability in nanocrystalline ferromagnets[J].IEEE Transactions on Magnetics,1990(5):1397-1402. |
| [6] | Allia P;Baricco M;Tiberto P et al.[J].Physical Review B,1993,47(06):3118. |
| [7] | 张茂才,周寿增,王亦忠,Hadjipanayis G C.铸造RE-Fe-（C,B）合金的组织结构与磁性[J].中国稀土学报,2001(05):411-413. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%