在阳/非离子表面活性剂及引发剂作用下,将甲基丙烯酸十二氟庚酯、甲基丙烯酸十二醇酯、丙烯酸羟丙酯、甲基丙烯酸二甲氨乙酯、乙烯基三乙氧基硅烷进行乳液共聚,制得了硅烷改性的阳离子氟代聚丙烯酸酯乳液(FL-HDV).用红外光谱(FT-IR)和核磁共振氢谱(1H NMR)对FLHDV主组分的结构进行了表征,用X射线光电子能谱仪(XPS)对乳液的成膜表面成分进行分析和表征,并讨论了硅烷改性前后及不同的整理工艺对其在涤纶织物上应用性能的影响.结果表明,与未用硅烷改性的氟代聚丙烯酸酯乳液(FLDH)对比,硅烷改性可以提高含氟聚合物的交联度,进而增加织物的拒水拒油性.XPS分析和接触角测定结果表明,在涤纶纤维表面明显存在有FLHDV膜,使得纤维与空气的界面上富集着疏水的含氟链段,而硅氧基团与纤维表面结合,从而赋予涤纶良好的拒水拒油性.在不同的工艺条件下,一浸一轧工艺处理的织物具有更高的拒水拒油等级,且弯曲刚度略低,柔软度较好.
参考文献
| [1] | 杨秦欢,李正军,张廷有.阳离子型含氟聚丙烯酸酯无皂乳液聚合的研究[J].皮革科学与工程,2009(01):5-8. |
| [2] | 肖新颜,刘健飞.核-壳结构含氟丙烯酸酯乳液的全盛与表征[J].中国化学工程学报(英文版),2008(04):626-630. |
| [3] | Huang PY;Chao YC;Liao YT .Enhancement of the water repellency durability of the fabrics treated by fluorinated nanocopolymer emulsions[J].Journal of Applied Polymer Science,2007(4):2451-2457. |
| [4] | 安秋凤,付永山,高金凤,李明涛,王前进.阳离子氟代聚丙烯酸酯乳液的制备及应用[J].精细化工,2008(04):392-396. |
| [5] | 王凌,胡望明.涤纶水刺非织造布的拒水整理与性能测试[J].纺织学报,2007(01):84-86. |
| [6] | 杜文琴,狄剑锋.建筑用拒水顶篷纺织材料研制及处理剂稳定性研究[J].中国纺织大学学报,2000(03):76-79. |
| [7] | YANG J X;PI P H;WEN X F et al.A novel method to fabricate superhydrophabic surfaces based on well-defined mulberry-like particles and self-assembly of peludimethylsiloxane[J].Applied Surface Science,2009,255:3507-3512. |
| [8] | Qu, AL;Wen, XF;Pi, PH;Cheng, J;Yang, ZR .Gradient distribution of fluorine on the film surface of the organic-inorganic hybrid fluoropolymer[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2009(1/3):18-25. |
| [9] | Qu A;Wen X;Pi P;Cheng J;Yang Z .Synthesis of composite particles through emulsion polymerization based on silica/fluoroacrylate-siloxane using anionic reactive and nonionic surfactants[J].Journal of Colloid and Interface Science,2008(1):62-69. |
| [10] | HUANG J Q;MENG W D;QING F L .Synthesis and repellent properties of vinylidene fluoride-containing pelyacrylates[J].Journal of Fluorine Chemistry,2007,128:1469-1477. |
| [11] | AATCC Test Method 22-2001.AATCC Technical Manual[S].,2004. |
| [12] | AATCC Test Method 118-2002.AATCC Technical Manual[S].,2004. |
| [13] | 邱俊英,程艳玲,郭小丽,熊圣东,易昌凤.有机氟硅改性丙烯酸酯共聚物乳液的研究[J].涂料工业,2008(08):37-39. |
| [14] | 魏海洋,贺文潇,粟小理,李欣欣,韩哲文.热处理对超疏水性含氟丙烯酸酯共聚物膜表面性能的影响[J].高等学校化学学报,2009(04):821-824. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%