以异佛尔酮二异氰酸酯(IPDI)、聚醚多元醇、二羟甲基丙酸(DMPA)和甲基丙烯酸甲酯(MMA)等为原料通过种子乳液聚合制得了水性聚氨酯-丙烯酸酯复合乳液,进一步配制成木器用水性聚氨酯-丙烯酸酯涂料.分别采用三羟甲基丙烷(TMP)和环氧树脂E-20作为内交联剂对聚合物进行改性.通过设计一系列配方,考察了两者对水性聚氨酯-丙烯酸酯涂料性能的影响.研究表明:在设计实验条件下,TMP对漆膜耐水、耐醇、耐污染性能改善效果不好,而E-20对漆膜各方而性能有显著提高.用5%～8%E-20改性的涂料性能能满足木器涂料的要求.
参考文献
| [1] | Hirose M.;Zhou JH.;Kadowaki F. .THE STRUCTURE AND PROPERTIES OF CORE-SHELL TYPE ACRYLIC-POLYURETHANE HYBRID AQUEOUS EMULSIONS [Review][J].Progress in Organic Coatings: An International Review Journal,1997(1/2):157-169. |
| [2] | UR(S)ka (S)BENIK;MATJA(Z) KRAJNC.Seeded semibatch emulsion copolymerization of methyl methacrylate and butyl acrylate using polyurethane dispersion:effect of soft segment length on kinetics[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2004(233):51-62. |
| [3] | Sebenik U;Krajnc M .Semibatch emulsion polymerization of methyl methacrylate using different polyurethane particles[J].Journal of Polymer Science, Part A. Polymer Chemistry,2005(4):844-858. |
| [4] | 王春艳,朱传方,万婷,陈晶晶.环氧改性脂肪族水性聚氨酯的合成与性能[J].应用化学,2006(04):441-443. |
| [5] | 黄先威,肖鑫,刘方,孔毅.环氧树脂改性水性聚氨酯的研究[J].聚氨酯工业,2005(02):20-23. |
| [6] | 瞿金清,陈焕钦.环氧改性水性聚氨酯涂料的合成与性能研究[J].高校化学工程学报,2002(05):570-574. |
| [7] | 黄洪,傅和青,邓艳文,陈焕钦.环氧树脂与丙烯酸酯复合改性水性聚氨酯的合成研究[J].高校化学工程学报,2006(04):583-587. |
| [8] | 王春会,李树材.环氧树脂改性水性聚氨酯的合成与性能研究[J].聚氨酯工业,2005(06):20-23. |
| [9] | 姜守霞,孙威,周照毅.环氧改性水性聚氨酯涂料的合成研究[J].应用化工,2003(05):17-21. |
| [10] | 邓朝霞,叶代勇,陈焕钦.影响环氧改性水性PUA乳液稳定性和耐水性的因素[J].陕西科技大学学报（自然科学版）,2006(05):24-30. |
| [11] | 瞿金清,陈焕钦.高固含量水性聚氨酯分散体的合成[J].化工学报,2003(06):868-871. |
| [12] | 黄玉科,瞿金清,杨卓如.水性聚氨酯耐水性的研究[J].涂料工业,2002(10):3-5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%