采用一步法,以 N,N-二(4-氨基苯基)-4-(十二烷氧基联苯基)-4’-氨基苯醚(C12-BAAPE)为控制预倾角的功能性二胺,2,2’-双三氟甲基-4,4’-联苯二胺(TFDB)或4,4’-二氨基二苯醚(ODA)为辅助二胺,分别与2,2’-双(3,4-二羧苯基)六氟丙烷四羧酸二酐(6FDA)和4,4’-联苯醚二酐(ODPA)聚合,得到三种主链结构不同的聚酰亚胺(PI-1、PI-2和PI-3)。利用 NMR、FT-IR、DSC、TGA、偏光显微镜和预倾角测试仪对聚合物的结构、热性能以及制备的液晶盒的取向性进行了表征,同时测试了3种 PI 的溶解性能。结果表明,PI-2液晶取向膜的耐摩擦性能明显优于 PI-1和 PI-3,且具有更高的玻璃化转变温度(T g )和分解温度(T d ),更好的溶解性能。分子模拟(MS)表明,由于 PI-2分子主链垂直构象的存在,增加了分子链的刚性,因而提高了取向膜的耐摩擦性能。
A series polyimides (PIs)were prepared by one-step method.These PIs were comprised of a functional diamine N,N-bis (4-aminophenyl )-4-(dodecylo-xy-biphenyl )-4′-amino-phenylether (C1 2 -BAAPE),one of two commercially available diamines 2,2′-Bis(trifluoromethy-l)-4,4′-diaminobiphe-nyl (TFDB),4,4′-Oxydianiline (ODA)and one of two dianhydride 4,4′-(hexafluoroisopropylidene) diphthalic anhydride (6FDA)and 4,4′-Oxydiphthalic anhydride (ODPA)in order to get different backbone structures.The structures and thermo properties of these PIs were characterized by NMR, FT-IR,DSC and TGA.Pretilt angles and alignment abilities were carried out by pretilt angle tester and polarization microscope.Solubility of PIs was tested by dissolving PIs in various organic solvents. DSC and TGA curves showed that PI-2 had higher glass transition temperature (T g )and decomposi-tion temperature (T d )than PI-1 and PI-3.Three PI films presented vertical alignment before mechan-ical rubbing and only PI-2 maintained it after rubbing process.Conformations of these PIs were simu-lated by Material Studio (MS).The vertical conformation existed in PI-2 ’s backbones improved rubbing resistance and showed vertical alignment ability after rubbing.
参考文献
| [1] | 袁泽明,杨玉叶,高锐敏,姚宁.现代显示技术的研究进展[J].现代显示,2008(11):18-21,57. |
| [2] | 刘晓那,宋勇志,徐长健,周波,马国靖,陈松飞,袁剑峰,林承武,邵喜斌.配向膜材料与面残影的关联性研究[J].液晶与显示,2014(03):317-321. |
| [3] | 刘志杰,卢鑫,汪映寒.液晶垂直取向膜材料的研究[J].高分子材料科学与工程,2007(02):19-23. |
| [4] | 丁孟贤.聚酰亚胺-化学、结构与性能的关系及材料[M].2 版.北京:科学出版社,2012. Ding M X.Polyimides-Relationship between Chemistry,Structures and Properties and Materials [M].2 nd ed. Beijing:Science Press,2012.(in Chinese),2012. |
| [5] | Chern Y T,Ju M H.Conformation of polyimide backbone structures for determination of the pretilt angle of liquid crystals [J].Macromolecules,2009,42(1):1 69-1 79.,2009. |
| [6] | Lee Y J,Kim Y W,Ha J D,et al.Synthesis and characterization of novel polyimides with 1-octadecyl side chains for liquid crystal alignment layers [J].Polymers for Advanced Technologies,2007,18(3):226-234.,2007. |
| [7] | Gong S M,Liu M,Xia S L,et al.Synthesis of novel soluble polyimides containing triphenylamine groups for liquid crystal vertical alignment layers [J].J ournal of Polymer Research,2014,21(9):542.,2014. |
| [8] | Li H S,Liu J G,Wang K,et al.Synthesis and characterization of novel fluorinated polyimides derived from 4,4’-【2,2,2-trifluoro-1-(3,5-ditrifluoro-methylphenyl)ethylidene】diphthalic anhydride and aromatic diamines [J].Poly-mer,2006,47(4):1443-1450.,2006. |
| [9] | Yang C P,Su Y Y,Guo W,et al.Synthesis and properties of novel fluorinated polynaphthalimides derived from 1, 4,5,8-naphthalenetetracarboxylic dianhydride and trifluoromethyl-substituted aromatic bis(etheramine)s [J].Eu-ropean Polymer J ournal,2009,45(3):721-729.,2009. |
| [10] | Li Z,Liu J,Gao Z,et al.Organo-soluble and transparent polyimides containing phenylphosphine oxide and triflu-oromethylmoiety:Synthesis and characterization [J].European Polymer J ournal,2009,45(4):1 139-1 148.,2009. |
| [11] | Banerjee S,Madhra M K,Salunke A K,et al.Synthesis and properties of fluorinated polyimides.3.Derived from novel 1,3-bis【3’-trifluoromethyl-4’(4”-amino benzoxy)benzyl】-benzene and 4,4-bis【3’-trifluoromethyl-4’(4-ami-nobenzoxy)benzyl】biphenyl [J].Polymer,2003,44(3):613-622.,2003. |
| [12] | Banerjee S,Madhra M K,Salunke A K,et al.Synthesis and properties of fluorinated polyimides.1.Derived from novel 4,4”-bis(aminophenoxy)-3,3”-trifluoromethyl terphenyl [J].J ournal of Polymer Science Part A:Polymer Chemistry,2002,40(8):101 6-1027.,2002. |
| [13] | Seo D S,Araya K,Yoshida N,et al.Effect of the polymer tilt angle for generation of pretilt angle in nematic liq-uid crystal on rubbed polyimide surfaces [J].J apanese J ournal of Applied Physics,1 995,34(4B):503-506.,1995. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%