以传统电子陶瓷工艺制备了(K0.5Na0.5)1-2xSrx(Nb0.94 Sb0.06)O3 无铅压电陶瓷,研究了适量锶、锑取代对陶瓷结构及电性能的影响. 结果表明,少量的锶、锑取代没有改变(K0.5Na0.5) NbO3陶瓷的相结构,仍为单相正交结构的钙钛矿型铁电体;适量的锶取代使得晶粒大小均匀一致,提高了陶瓷的致密度;锶、锑取代降低了陶瓷的居里温度,但对正交四方相变温度的影响不大,且在0~200℃的温度范围,介电常数几乎不依赖频率的变化而变化;在x=0.008处,得到较好综合性能的陶瓷材料:d33=155pC/N,kp=0.361,Qm=120,Np=2862,Pr=23μC/cm2Ec=1.4kV/mm,ρ=4.411g/cm3.

Leadfree piezoelectric ceramics (K0.5Na0.5)1-2xSrx(Nb0.94 Sb0.06)O3 (abbreviated as KNSNS1000x) were synthesized by the conventional ceramic sintering technique. The structure and electrical properties of KNSNS1000x ceramics were investigated. The results of XRD indicate that KNSNS1000x ceramics have an orthorhombic structure. The proper content of Sr substitute increases the density of ceramics which reaches the maximum value of 4.411g/cm3 at x=0.008. With the increase of the amount of Sr, the Tc decreases and the temperature of orthorhombictetragonal phase transition (To-t) is almost a constant.In the temperature range from 0℃ to 200℃, dielectric constant of KNSNS1000x ceramics is independent of frequency. The KNSNS8 ceramics obtains the optimum piezoelectric properties: d33=155pC/N, kp=0.361,Qm=120,Np=2862,Pr=23μC/cm2Ec=1.4kV/mm,ρ=4.411g/cm3.

参考文献

[1] ]Shirane G, Newnham R, Pepinsky R. Physical Review, 1954, 96(3): 581-588.
[2]Egerton L, Dillon D M. J. Am. Ceram. Soc., 1959, 42(9): 438-442.
[3]Matsubara M, Yamaguchi T, Sakamoto W, et al. J. Am. Ceram. Soc., 2005, 88(5): 1190-1196.
[4]Saito Y, Takao H. Nature, 2004, 432(4): 84-87.
[5]Jaeger R E, Egerton L. J. Am. Ceram. Soc., 1962, 45(5): 209-213.
[6]Li J F, Wang K. J. Am. Ceram. Soc., 2006, 89(2): 706-709.
[7]Guo Y P, Kakimoto K I, Ohsato H. Jpn. J. Appl. Phys., 2004, 43(9B): 6662-6666.
[8]Zuo R Z, Fang X S, Ye C. J. Am. Ceram. Soc., 2007, 90(8): 2424-2428.
[9]Cho K H, Park H Y, Ahn C W, et al. J. Am. Ceram. Soc., 2007, 90(6): 1946-1949.
[10]唐福生,杜红亮,刘代军,等(TANG FuSheng, et al).无机材料学报(Journal of Inorganic Materials),2007, 22(2): 321-325.
[11]Park S H, Ahn C W, Nahm S, et al. Jpn. J. Appl. Phys., 2004, 43(8B): L1072-L1074.
[12]郑立梅,王矜奉,臧国忠,等. 电子元件与材料,2006, 25(7): 21-22.
[13]Zhou R Z, Rodel J, Chen R Z, et al. J. Am. Ceram. Soc., 2006, 89(6): 2010-2015.
[14]吴 玲,任晓峰,张家良,等. 四川大学学报(自然科学版),2005, 42: 300-304.
[15]Lin D M, Kwok K W, Tian H Y, et al. J. Am. Ceram. Soc., 2007, 90(5): 1458-1462.
[16]Tashiro S, Nagamatsu H, Nagata K. Jpn. J. Appl. Phys., 2002, 41(11B): 7113-7118.
[17]Tashiro S, Ishii K. J. Ceram. Soc. Jpn., 2006, 114(5): 386-391.
[18]刘 涛,丁爱丽,何夕云,等(LIU Tao, et al). 无机材料学报(Journal of Inorganic Materials),2007, 22(3): 470-474.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%