采用循环伏安法,在含吡咯和苯胺的0.3 mol/L草酸水溶液中制备了聚吡咯/聚苯胺(PPy/Pani)的复合型导电聚合膜.采用红外光谱、极化曲线、自腐蚀电位-时间曲线、扫描电子显微镜和电化学阻抗谱研究了共聚膜的防腐蚀性能.结果表明,在1 mol/L H2SO4中,PPy、Pani与不锈钢基体发生氧化还原反应,促进不锈钢表面发生钝化；当苯胺与吡咯浓度比为1∶3时,制备得到的复合型导电聚合膜所保护的不锈钢自腐蚀电流最小,自腐蚀电位最高,保护时间最长.PPy、Pani及其共聚膜在3.5％ NaCl溶液中电化学阻抗谱表明,所制备的PPy、Pani及其共聚物膜与不锈钢基体发生氧化还原反应,使其表面钝化；当Cl-到达不锈钢表面时,破坏钝化膜导致不锈钢腐蚀.
参考文献
| [1] | MacDiarmid A G.Polyaniline and Polypyrrole:Where Are We Headed[J].Synth Met,1997,84:27-34. |
| [2] | Deberry D W.Modification of the Electrochemical and Corrosion Behavior of Stainless Steels with an Electroactive Coating[J].J Electrochem Soc,1985,132(5):1022-1026. |
| [3] | West K,Jacobsen T,Zachan-Christiansen B,et al.Electrochemical Synthesis of Polypyrrole:Influence of Current Density on Structure[J].Synth Met,1993,55 (2/ 3):1412-1417. |
| [4] | LI Yongfang.Conducting Polymers[J].Prog Chem,2002,14(3):207-211 (in Chinese).李永舫.导电聚合物[J].化学进展,2002,14(3):207-211. |
| [5] | XIAO Yinghong,WANG Jing,SUN Xiaoliang,et al.Electrochemical Behavior and Surface Morphology of Conducting Polypyrrole[J].J Nanjing Univ Sci Technol(Nat Sci Ed),2005,29 (4):483-485(in Chinese).肖迎红,王静,孙晓亮,等.导电聚吡咯的电化学行为及表面形貌研究[J].南京理工大学学报(自然科学版),2005,29(4):483-485. |
| [6] | LI Yongfang.Studies on Conducting Polypyrrole[J].Polym Bull,2005,(4):51-57(in Chinese).李永舫.导电聚吡咯的研究[J].高分子通报,2005,(4):51-57. |
| [7] | XIE Fazhi,XUAN Han.Synthesis and Inhibiting Performance of an Imidazolinyl-quaternary Ammonium Salts Inhibitor with Multi-activated Sites[J].Chinese J Appl Chem,2011,28(1):94-100(in Chinese).谢发之,宣寒.多点位吸附型咪唑啉季铵盐缓蚀剂的合成及其缓蚀性能[J].应用化学,2011,28(1):94-100. |
| [8] | XU Hui,WANG Xinying,LIU Xiaoyu.Preparation and Performance of Composite Film of PANI/PPY[J].Corros Sci Prot Technol,2012,24(2):127-131(in Chinese).徐慧,王新颖,刘小育.聚苯胺/聚吡咯复合薄膜的制备及其抗腐蚀性能研究[J].腐蚀科学与防护技术,2012,24(2):127-131. |
| [9] | Lim V W L,Kang E T,Neoh K G.Determination of Pyrrole-aniline Copolymer Compositions by X-ray Photoelectron Spectroscopy[J].Appl Surf Sci,2001,181(3/4):317-326. |
| [10] | Bekir S,Muzaffer T.Electrochemical Copolymerization of Pyrrole and Aniline[J].Synth Met,1998,94(2):221-227. |
| [11] | Park Y H,Kim K W,Baik D H,et al.Electrochemical Polymerization and Characterization of Conducting Copolymers from Pyrrole and Poly(acryloyl chloride)[J].Mol Cryst Liq Cryst,2002,(377):361-364. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%