采用四甲基苯二甲基二异氰酸酯、聚酯二元醇和二羟甲基丙酸为原料,合成了一系列具有不同异氰酸根与羟基摩尔比(n(-NCO)/n(-OH))的聚氨酯乳液.研究了n(-NCO)/n(-OH)对水性聚氨酯性能的影响.结果表明,当该比值增加时,乳液的粒径增大,分布变宽,结晶性降低,耐热性下降,耐水性能呈现降低的趋势.当异氰酸根与羟基摩尔比为3时,四甲基苯二甲基二异氰酸酯基水性聚氨酯的乳液粒径为10～30nm,膜的分解温度达到275℃,24h吸水率低于10％.
参考文献
| [1] | Du H,Zhao Y H,Li Q F,et al.Synthesis and Characterization of Waterborne Polyurethane Adhesive from MDI and HDI[J].J Appl Polym Sci,2008,110(3):1396-1402. |
| [2] | Borja F A,Lorena R,Koro C,et al.Composition and Properties Differences of Biodegradable Polyurethanes Based on MDI and HDI[J].Polym Eng Sci,2008,48(3):519-529. |
| [3] | Yang C H,Yang H J,Wen T C,et al.Mixture Design Approaches to IPDI-H6XDI-XDI Ternary Diisocyanatebased Waterborne Polyurethanes[J].Polymer,1999,40(4):871-885. |
| [4] | SUN Yanpu,REN Xiaoxiu.Low Viscosity Waterborne Polyurethane Prepolymer[J].Paint Coat Ind,2003,33(4):32-34,60(in Chinese).孙彦璞,任孝修.低粘度水性聚氨酯预聚体[J].涂料工业,2003,33(4):32-34,60. |
| [5] | SUN Yanpu.Influence of Activity of Terminal OH Group of Polyester Diol on Mechanical Properties of Polyester-Based WPU[J].Paint Coat Ind,2009,39(2):15-18(in Chinese).孙彦璞.聚酯二醇端羟基活性对聚酯型水性聚氨酯力学性能的影响[J].涂料工业,2009,39(2):15-18. |
| [6] | SUN Yanpu.Study on Partical Size Distribntion of Polyester-Based Waterborne Polyurethane(WPU) Emulsion and Water Resistance of The Film[J].Paint Coat Ind,2010,40(3):32-35(in Chinese).孙彦璞.聚酯型水性聚氨酯乳液粒径分布及乳液膜耐水性的研究[J].涂料工业,2010,40(3):32-35. |
| [7] | YE Qingxuan.Application of TMXDI in the Aqueous Polyurethanes[J].Chem Propell Polym Mater,2005,3(5):5-7(in Chinese).叶青萱.TMXDI在水性聚氨酯中的应用[J].化学推进剂与高分子材料,2005,3(5):5-7. |
| [8] | Suzana M C,Jakov V S,Dragan M D,et al.Synthesis and Degradation Profile of Cast Films of PPG-DMPA-IPDI Aqueous Polyurethane Dispersions Based on Selective Catalysts[J].Polym Degrad Stab,2009,94(11):2015-2022. |
| [9] | WANG Chunyan,ZHU Chuanfang,WAN Ting,et al.Synthesis and Properties of a Waterborne Aliphatic Polyurethane Modified by Epoxy Resin[J].Chinese J Appl Chem,2006,23(4):441-443(in Chinese).王春艳,朱传方,万婷,等.环氧改性脂肪族水性聚氨酯的合成与性能[J].应用化学,2006,23(4):441-443. |
| [10] | Jiang X,Li J H,Ding M M,et al.Synthesis and Degradation of Nontoxic Biodegradable Waterborne Polyurethanes Elastomer with Poly((ε)-caprolactone) and Poly(ethylene glycol) as Soft Segment[J].Eur Polym J,2007,43(5):1838-1846. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%