以Fe(NO3)3·9H2O、LiNO3、NH4H2PO4和蔗糖为原料,在超临界CO2流体中反应合成,进而经二次焙烧制得LiFePO4/C.结果表明,在超临界CO2流体中经50 ℃反应24 h,在350和600 ℃焙烧后制得粒径分布在0.5～1.0μm的纯LiFePO4/C,该材料作为锂离子电池正极的放电比容量达156.6 mA·h/g,经50次循环后容量几乎没有衰减.
参考文献
| [1] | Padhi A K,Nanjundaswamy K S,Goodenough J B.J Electrochem Soc[J],1997,144:1188 |
| [2] | Hu Y S,Guo Y G,Dominko R,Gaberscek M,Maier J,Jamnik J.Adv Mater[J],2007,19:1963 |
| [3] | Croce F,Epifanio A D,Hassoun J,Deptula A,Olczac T,Scrosati B.Electrochem Solid-State Lett[J],2002,5:A47 |
| [4] | Park K S,Schougaard S B,Goodenough J B.Adv Mater[J],2007,19:848 |
| [5] | Chung S Y,Bloking J T,Chiang Y M.Nat Mater[J],2002,1:123 |
| [6] | Wang Y G,Wang Y R,Hosono E,Wang K X,Zhou H.Angew Chem Int Ed[J],2008,47:7461 |
| [7] | Dominko R,Bele M,Gaberscek M,Remskar M,Hanzel D,Goupil J M,Pejovnik S,Jamnik J.J Power Sources[J],2006,153:274 |
| [8] | Murugan A V,Muraliganth T,Ferreira P J,Manthiram A.Inorg Chem[J],2009,48(3):946 |
| [9] | Yang H,Wu X L,Cao M H,Guo Y G.J Phys Chem C[J],2009,113(8):3345 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%