采用溶胶-凝胶法,在FTO(SnO2:F)低辐射镀膜玻璃衬底上制备了柱状晶体结构的TiO2薄膜,获得双层结构FTO/TiO2镀膜玻璃样品.研究了TiO2薄膜厚度对FTO/TiO2镀膜玻璃样品的光催化活性、低辐射性能以及透光性能的影响.结果表明,FTO/TiO2镀膜玻璃样品光催化活性随着TiO2薄膜厚度的增加先升高后下降,在TiO2薄膜厚度为300 nm时光催化活性最佳;低辐射性能随着TiO2薄膜厚度的增加而下降,但TiO2薄膜厚度为300 nm时仍然具备一定的低辐射性能；透光性能与TiO2薄膜膜厚的关系不大,可见光透射比保持在72％左右；表面平均粗糙度约为1 nm,表面光滑,不易沾染油污灰尘.该镀膜玻璃在保证低辐射建筑节能和透光的前提下,兼具光催化自清洁功能,具有很好的应用前景.
参考文献
| [1] | Mavrodiev G,Gajdardziska M,Novkovski N.Properties of SnO2:F films prepared on glass substrates by the spraying method.Thin Solid Films,1984,113(2):93-100. |
| [2] | Fujishima A,Honda K.Electrochemical photolysis of water at a semiconductor electrode.Nature,1972,238:37-38. |
| [3] | Hoffmann M R,Marlin S T,Choi W Y,et al.Environmental applications of semiconductor photocatalysis.Chem.Rev.,1995,95(1):69-96. |
| [4] | Linsebigler A L,Lu G Q,Yates J T Jr.Photocatalysis on TiO2 surfaces:principles,mechanisms,and selected results.Chem.Rev.,1995,95(3):735-758. |
| [5] | Sopyan I,Watanabe M,Mumsawa S.Efficient TiO2 powder and film photocatalysts with rutile crystal structure.Chem.Lett.,1996,1:69-70. |
| [6] | Torimoto T,Ito S,Kuwabata S,et al.Effects of adsorbents used as supports for titanium dioxide loading on photocatalytic degradation of propyzamide.Environ.Sci.Technol.,1996,30(4):1275-1281. |
| [7] | SU Li-Cheng,CHU Cheng-Lin,DONG Yin-Sheng,et al.N-dopedTiO2 immobilized on nickel foam and its photocatalytic performance for formaldehyde degradation under visible light.Journal of Inorganic Materials,2010,25(7):753-757. |
| [8] | 宋晨路,刘军波,翁伟浩,等(SONG Chen-Lu,et al).常压化学气相沉积法制备氟掺杂TiO2自清洁薄膜.硅酸盐学报(Journal of the Chinese Ceramic Society),2010,1(38):58-63. |
| [9] | Bui Duc-Nguyen,Kang Shi-Zhao,Li Xiang-qing,et al.Effect of Si doping on the photocatalytic activity and photoelectrochemical property of TiO2 nanoparticles.Catalysis Communications,2011,13(1):14-17. |
| [10] | LI Xiao-Bin,LU Xiao-Hua.Microwave heating preparation of Ag modified TiO2 for photocatalytic degradation of gaseous toluene.Journal of Inorganic Materials,20 10,25(4):365-369. |
| [11] | TANG Yi-Wen,CHEN Zhi-Gang,ZHANG Li-Sha,etal.Preparation and characterization of nanocrystalline Cu2O/TiO2 heterojunction film electrode.Journal of Inorganic Materials,2006,21(2):453-458. |
| [12] | Yan Jian-hui,Zhang Li,Yang Hai-hua,et al.CuCr2O4/TiO2 heterojunctionfor photocatalytic H2evolution under simulated sunlight irradiation.Solar Energy,2009,83(9):1534-1539. |
| [13] | Okada M,Yamada Y,Jim Ping,et al.Fabrication of multifunctional coating which combines low-e property and visible-light-responsive photocatalvtic activity.Thin Solid Films,2003,442(1/2):217-221. |
| [14] | 林明贤,赵高凌,汪建勋,等(LIN Ming-Xian,et al).基板温度对常压化学气相沉积法制备TiO2复合薄膜性能的影响.硅酸盐学报(Journal of the Chinese Ceramic Society),2007,35(11):1520-1525. |
| [15] | Elangovan E,Ramamurthi K.A study on low cost-high conducting fluorine andantimony-doped tin oxide thin films.Applied Surface Science,2005,249(1-4):183-196. |
| [16] | XIAO Peng,ZHANG Yun-Huai,ZHANG Xiao-Xing,et al.Fabrication and characterization of transparent super-long titania nanotube arrays/FTO electrode.Journal oflnorganic Materials,2010,25(1):32-36. |
| [17] | 刘恩科,朱秉升,罗晋生,等.半导体物理学,6版.北京:电子工业出版社,2003:148-172. |
| [18] | 陈庭金,刘祖明,涂洁磊.多晶硅太阳电池的表面和界面复合.太阳能学报,2000,21(2):133-139. |
| [19] | Tachibana Y,Hara K,Sayama K,et al.Quantitative analysis of light-harvesting efficiency and electron-transfer yield in rutheinum-dye-sensitized nanocrystalline TiO2 solar cells.Chem.Mater.,2002,14(6):2527-2535. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%