对Al-Bi偏晶点成分合金(Al-3.4％Bi,质量分数)开展了逆重力方向的定向凝固实验,考察了凝固速度对合金凝固组织的影响,分析了试样凝固组织形成过程.结果表明:A1-Bi偏晶点成分合金定向凝固时在固-液界面前沿液相内形成溶质Bi富集层,并发生液-液相变,少量相液滴在Marangoni迁移、Stokes沉积和试样自身下拉运动共同作用下进行空间迁移,当凝固速度较快时,凝固界面前沿所有尺寸的少量相液滴均向凝固界面迁移,合金凝固后少量相粒子尺寸呈现单峰分布;当试样凝固速度较慢时,部分少量相液滴在长大过程中其合速度方向按:指向凝固界面-背离凝固界面-再指向凝固界面顺序随液滴尺寸变化,合金凝固后少量相粒子尺寸分布呈现2个峰;当凝固速度较快时,少量相粒子平均尺寸〈R〉随凝固速度V0近似呈〈R〉∞ V0-1/2指数关系变化,随着凝固速度的下降,〈R〉与V0间的关系向〈R〉∞V0-1/3指数关系趋近.
参考文献
| [1] | Jia J,Zhao J Z,Guo J J,Liu Y.Preparation Techniques of ImmiscibleAlloy Harbin:Harbin Institute of Technology Press,2002:2(贾均,赵九州,郭景杰,刘源.难混溶合金及其制备技术.哈尔滨:哈尔滨工业大学出版社,2002:2) |
| [2] | Pratt G C.IntMetRev,1973; 18:62 |
| [3] | Guo J J,Gui H B,Su Y Q,Bi W S,Jia J,Fu H Z.Spec Cast Nonfer Alloys,2004; 1:1(郭景杰,崔红保,苏彦庆,毕维生,贾均,傅恒志.特种铸造及有色合金,2004; 1:1) |
| [4] | Zheng H X,Xie H,Chen Z L,Yang G C,Guo X F.Chin J Nonferrous Met,2002; 26:15(郑红星,谢辉,陈倬麟,杨根仓,郭学峰.稀有金属,2002; 26:15) |
| [5] | Zhu D,Yang X H,Han X J,Wei B B.Chin J Nonferrous Met,2003; 13:328(朱定,杨晓华,韩秀君,魏炳波.中国有色金属学报,2003; 13:328) |
| [6] | Rudrakshi G B,Srivastava V C,Pathak J P,Ojha S N.Mater Sci Eng,2004; A383:30 |
| [7] | Liu Y,Guo J J,Jia J.Foundry,2000; 49:11(刘源,郭景杰,贾均.铸造,2000; 49:11) |
| [8] | Carlberg T,Fredriksson H.Metall Trans,1980; 11 A:1665 |
| [9] | Zhang H W,Xian A P.Acta Metall Sin,1999; 35:1187(张宏闻,冼爱平.金属学报,1999;35:1187) |
| [10] | Yang S,Liu W J.JMater Sci,2001; 36:5351 |
| [11] | Zhao J Z,Ratke L.ScrMater,1988; 39:181 |
| [12] | Zhao J Z,HuZ Q.Acta Metall Sin,2004; 40:27(赵九洲,胡壮麒.金属学报,2004; 40:27) |
| [13] | Cui H B,Guo J J,SuY Q,Wu S P,Li X Z,Fu H Z.Acta Metall Sin,2007; 43:907(崔红保,郭景杰,苏彦庆,吴士平,李新中,傅恒志.金属学报,2007; 43:907) |
| [14] | Zhao J Z.Scr Mater,2006; 54:247 |
| [15] | He J.PhD Dissertation,Institute of Metal Research,Chinese Academy of Sciences,Shenyang,2006(何杰.中国科学院金属研究所博士学位论文,沈阳,2006) |
| [16] | Yang S,Liu W J,Jia J.Prog Nat Sci,2001; 11:729(杨森,刘文今,贾均.自然科学进展,2001; 11:729) |
| [17] | Zhao J Z,Guo J J,Jia J,Li Q C.Chin JNonferrous Met,1994; 4(suppl):164(赵九洲,郭景杰,贾均,李庆春.中国有色金属学报,1994;4(增刊):164) |
| [18] | Zhao J Z,Li H L,Zhao L.Acta Metall Sin,2009; 45:1435(赵九洲,李海丽,赵雷.金属学报,2009; 45:1435) |
| [19] | Zhao J Z.Mater Sci Technol,2001; 9:154 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%