利用基于密度泛函理论的第一性原理计算了γ-TiAl (100)表面附近空位、Si和W掺杂的形成能,以及它们对O原子在该表面附近吸附和扩散的影响.计算结果表明,在掺杂体系中,Si原子更容易替代表面第1层Al原子的位置,而W原子更容易替代表面第2层Ti原子的位置,且2者均使其近邻吸附O原子的吸附能升高.因此,Si更容易偏析在表面第1层上,而W更容易偏析在表面第2层上,且抑制了O原子在γ-TiAl (100)表面的吸附.在空位缺陷体系中,表面第1层Ti原子空位比Al原子空位更易形成.在干净表面、Ti空位表面、Si掺杂和W掺杂表面体系中,O原子从表面上到表面下第2层扩散的能垒分别为1.98,1.34,2.53和2.69 eV,相对于干净表面,Ti空位缺陷的形成使得O原子在γ-TiAl (100)表面附近的扩散更加容易,而Si和W掺杂使得O原子在γ-TiAl(100)表面上的扩散更加困难.
参考文献
| [1] | Kim Y W.JOM,1994; 46(7):30 |
| [2] | Yamaguchi M,Umakoshi Y.Prog Mater Sci,1990; 34(1):1 |
| [3] | Yamaguchi M,Inui H,Ito K.Prog Mater Sci,2000; 48:307 |
| [4] | Loria E A.Intermetallics,2001; 9:997 |
| [5] | Froes F H,Suryanarayana C,Eliezer D.J Mater Sci,1992;27:5113 |
| [6] | Clemens H,Kestler H.Adv Eng Mater,2000; 2:551 |
| [7] | Lang C,Schütze M.Oxid Met,1996; 46:255 |
| [8] | Lang C,Schütze M.Mater Corros,1997; 48(1):13 |
| [9] | Rahmel A,Quadakkers W J,Schütze M.Mater Corros,1995; 46:217 |
| [10] | Taniguchi S,Juso H,Shibata T.Oxid Met,1998; 49:325 |
| [11] | Toshio N,Takeshi I,Mamoru Y,Takayuki Y.Intermetallics,2000; 8:371 |
| [12] | Taniguchi S,Zhu Y C,Kazuhisa F,Nobuya I.Oxid Met,2002; 58:375 |
| [13] | Shida Y,Anada H.Mater Trans,1994; 35:623 |
| [14] | Kim B G,Kim G M,Kim C J.Scr Metall Mater,1995;33:1117 |
| [15] | Taniguchi S,Uesaki K,Zhu Y C,Matsumoto Y,Shibata T.Mater Sci Eng,1999; A266:267 |
| [16] | Taniguchi S,Kuwagawa T,Zhu Y C,Matsumoto Y,Shibata T.Mater Sci Eng,2000; A277:229 |
| [17] | Li H,Liu L M,Wang S Q,Ye H Q.Acta Metall Sin,2006;42:897(李虹,刘利民,王绍青,叶恒强.金属学报,2006; 42:897) |
| [18] | Liu S Y,Shang J X,Wang F H,Zhang Y.J Phys Condens Matter,2009; 21:225005 |
| [19] | Song Y,Dai J H,Yang R.Surf Sci,2012; 606:857 |
| [20] | Wang L,Shang J X,Wang F H,Zhang Y,Chroness A.J Phys Condens Matter,2011; 23:265009 |
| [21] | Wang L,Shang J X,Wang F H,Zhang Y.Acta Mater,2012; 61:1726 |
| [22] | Kresse G,Hafner J.Phys Rev,1993; 48B:13115 |
| [23] | Blochl P E.Phys Rev,1994; 50B:17953 |
| [24] | Monkhorst H J,Pack J D.Phys Rev,1976; 13B:5188 |
| [25] | Perdew J P,Chevary J A,Vosko S H,Jackson K A,Pederson M R,Singh D J,Fiolhais C,Phys Rev,1992; 46B:6671 |
| [26] | Brandes E A.Smithell Metals Reference Book.6Ed.,United Kingdom:Butterworths,1983:1 |
| [27] | Liu S Y,Shang J X,Wang F H,Zhang Y.Phys Rev,2009;79B:075419 |
| [28] | Henkelman G,Uberuaga B P,Jonsson H.J Chem Phys,2000; 113:9901 |
| [29] | Kohn W,Sham L J.Phys Rev,1965; 140:A1133 |
| [30] | Zhao C Y.Master Thesis,Capital Normal University,Beijing,2012(赵春英.首都师范大学硕士学位论文,北京,2012) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%