针对模拟初始组织的变化,对局域自由能密度函数的表达式进行了改进,建立了纳米尺度下晶界作用域的取值模型,由此考察确定了各模拟参数物理意义的取值,建立了纳米尺度模拟晶粒生长的相场模型.模拟研究了真实时空下多晶AZ31镁合金纳米晶粒生长过程,与实验报道数据进行了比较,模拟结果与实验数据吻合较好；还与常规微米尺度的晶粒生长模拟结果进行了对比,探讨了纳米尺度下微观组织的演变机制.模拟结果显示:纳米晶的晶界作用域覆盖了相邻的2个纳米晶粒；界面能约为微米晶界面能的一半,纳米晶的界面偏析更严重.这可能是使纳米晶界面能动性降低,从而导致晶粒初期生长速度低的原因.通过定量模拟研究纳米晶的混晶情况发现,纳米尺度混晶度的增幅比微米尺度更明显.
参考文献
| [1] | Siegel R W,Fougere G E.Nanostruct Mater,1995; 6:205 |
| [2] | Youssef K,Scattergood R,Murty K,Koch C.Scr Mater,2006; 54:251 |
| [3] | Hao Y L,Yang R.Acta Metall Sin,2005; 41:1183(郝玉琳,杨锐.金属学报,2005; 41:1183) |
| [4] | Zong Y P,Wang M T,Guo W.Acta Phys Sin,2009; 58:S161(宗亚平,王明涛,郭巍.物理学报,2009; 58:S161) |
| [5] | Wang M,Zong B Y,Wang G.Comput Mater Sci,2009;45:217 |
| [6] | Wang M T,Zong Y P,Wang G.ChinJ Nonferrous Met,2009; 19:1555(王明涛,宗亚平,王刚.有色金属学报,2009; 19:1555) |
| [7] | Wu Y,Zong B Y,Wang M T.Mater Sci Forum,2010;633:697 |
| [8] | Zhang X G,Zong Y P,Wang M T,Wu Y.Acta Phys Sin,2011; 60:068201(张宪刚,宗亚平,王明涛,吴艳.物理学报,2011; 60:068201) |
| [9] | Zhang X G,Zong Y P,Wu Y.Acta Phys Sin,2012; 61:088104(张宪刚,宗亚平,吴艳.物理学报,2012; 61:88104) |
| [10] | Karma A,Rappel W J.Phys Rev,1996; 53E:3017 |
| [11] | Wen Y,Wang B,Simmons J,Wang Y.Acta Mater,2006;54:2087 |
| [12] | Allen S M,Cahn J W.Acta Metall,1979; 27:1085 |
| [13] | Cahn J W,Hilliard J E.J Chem Phys,1958; 28:258 |
| [14] | Krill Ⅲ C,Chen L Q.Acta Mater,2002; 50:3059 |
| [15] | Nishizawa T,translated by Hao S M.Thermodynamics of Microstructure.Beijing:Chemical Industry Press,2006:136(Nishizawa T著,郝士明译.微观组织热力学.北京:化学工业出版社,2006:136) |
| [16] | Shek C,Lai J,Lin G.Nanostruct Mater,1999; 11:887 |
| [17] | Fan D,Geng C,Chen Q.Acta Mater,1997; 45:1115 |
| [18] | Liu Z,Liang W,Xu B S,Ichinose H.Mater Sci Technol,2000; 8:103(刘珍,梁伟,许并社,市野濑英喜.材料科学与工艺,2000;8:103) |
| [19] | Deng C.Master Thesis,Harbin Institute of Technology,2009(邓澄.哈尔滨工业大学硕士学位论文,2009) |
| [20] | Gjostein N,Rhines F.Acta Metall,1959; 7:319 |
| [21] | Van Swygenhoven H,Farkas D,Caro A.Phys Rev,2000;62B:831 |
| [22] | Wang J Q,Geng P,Zeng M G,Zhang B J,Qian C F.Chin J Mater Res,1997; 11:316(王建强,耿平,曾梅光,张宝金,钱存富.材料研究学报,1997;11:316) |
| [23] | Zhang Y,Tao N,Lu K.Acta Mater,2008; 56:2429 |
| [24] | Wen Y,Simmons J,Shen C,Woodward C,Wang Y.Acta Mater,2003; 51:1123 |
| [25] | Hillert M.Acta Metall,1965; 13:227 |
| [26] | Liu R C,Wang L Y,Gu L G,Huang G S.Light Alloy Fabric Technol,2004; 32:22(刘饶川,汪凌云,辜蕾刚,黄光胜.轻合金加工技术,2004; 32:22) |
| [27] | Michels A,Krill C,Ehrhardt H,Birringer R,Wu D.Acta Mater,1999; 47:214 |
| [28] | F(a)rber B,Cadel E,Menand A,Schmitz G,Kirchheim R.Acta Mater,2000; 48:789 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%