对Fe-22Mn-3Si-2Al高锰TRIP/TWIP钢拉伸变形后的组织、性能特点进行研究,利用EBSD技术分析了形变过程中马氏体相变的晶体学特点.结果表明,Fe-22Mn钢形变前含有大量硬度高于奥氏体的热致ε-M；拉伸变形后,热致ε-M转变为α′-M,ε-M与α′-M相变有明显的先后顺序,即具有不同步性.Fe-22Mn钢拉伸时TRIP效应和TWIP效应共存,具有良好的塑性和强度结合,且ε-M没有引起低温脆性.热致ε-M为倾转的基面取向,形变时易发生基面滑移,并发生少量86°〈11(2)0〉孪晶,在出现30°〈0001〉误标后与ε-M基体形成93°〈(7)253〉取向关系.形变后α′-M取向绕〈110〉转动,变得漫散,形成“彗星拖尾”现象.同时,形变过程中奥氏体的取向也发生转动,产生绕〈110〉轴的小角度取向差.此外,原始奥氏体中的大量退火孪晶界对马氏体相变有促进作用.
参考文献
| [1] | Gr(a)ssel O,Kriiger L,Frommeyer G,Meyer L W.Int J Plast,2000; 16:1391 |
| [2] | Schumann V H.Neue Hütte,1972; 17:605 |
| [3] | Saeed-Akbari A,Imlau J,Prahl U,Bleck W.Metall Mater Trans,2009; 40A:3076 |
| [4] | Allain S,Chateau J-P,Bouaziz O,Migot S,Guelton N.Mater Sci Eng,2004; A387-389:158 |
| [5] | Dumay A,Chateau J-P,Allain S,Migot S,Bouaziz O.Mater Sci Eng,2008; A483-484:184 |
| [6] | Frommeyer G,Brux U,Neumann P.ISIJ Int,2003; 3:438 |
| [7] | Bracke L,Kestensa L,Penning J.Scr Mater,2007; 57:385 |
| [8] | Mina X H,Sawaguchi T,Ogawa K,Maruyama T,Yin F X,Tsuzaki K.Mater Sci Eng,2011; A528:5251 |
| [9] | Chun Y S,Kim J S,Park K-T,Lee Y-K,Lee C S.Mater Sci Eng,2012; A533:87 |
| [10] | Kirindi T,Dikici M.J Alloys Compd,2006; 407:157 |
| [11] | Bergeon N,Guenin G,Esnouf C.Mater Sci Eng,1998;A242:87 |
| [12] | Wu X,Tao N,Hong Y,Lu J,Lu K.Scr Mater,2005; 52:547 |
| [13] | Yang H S,Bhadeshia H K D H.Scr Mater,2009; 60:493 |
| [14] | Lu F Y,Yang P,Meng L,Cui F E,Ding H.J Mater Sci Technol,2011; 27:257 |
| [15] | Lii Y P,Hutchinson B,Molodov D A,Gottstein G.Acta Mater,2010; 58:3079 |
| [16] | Koyama M,Sawaguchi T,Lee T,Lee C S,Tsuzaki K.Mater Sci Eng,2011; A528:7310 |
| [17] | Datta K,Delhez R,Bronsveld P M,Beyer J,Geijselaers H J M,Post J.Acta Mater,2009; 57:3321 |
| [18] | Hedstr(o)m P,Lienert U,Almer J,Odén M.Mater Lett,2008; 62:338 |
| [19] | Wu C-C,Wang S-H,Chen C Y,Yang J-R,Chiu P-K,Fang J.Scr Mater,2007; 56:717 |
| [20] | Yang P,Lu F Y,Meng L,Cui F E.Acta Metall Sin,2010;46:657(杨平,鲁法云,孟利,崔凤娥.金属学报,2010; 46:657) |
| [21] | Yang P,Lu F Y,Meng L,Cui F E.Acta Metall Sin,2010;46:666(杨平,鲁法云,孟利,崔凤娥.金属学报,2010; 46:666) |
| [22] | Liu T Y,Yang P,Meng L,Lu F Y.J Alloys Compd,2011;509:8337 |
| [23] | Yang P,Liu T Y,Lu F Y,Meng L.Steel Res Int,2012;83:368 |
| [24] | Barbier D,Gey N,Allain S,Bozzolo N,Humbert M.Mater Sci Eng,2009; A500:196 |
| [25] | Jin J E,Lee Y K.Mater Sci Eng,2009; A527:157 |
| [26] | Beladi H,Timokhina I B,Estrin Y,Kim J,De Cooman B C,Kim S K.Acta Mater,2011; 59:7787 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%