将Q235碳钢在流动海水中浸泡280 d,利用失重法和多种腐蚀电化学方法研究了其在浸泡过程中的腐蚀规律.结果表明,与静止海水浸泡相比,在流动体系长时间浸泡后,电极表面几乎不存在疏松的黄色锈层,而被一层致密的黑色腐蚀产物所覆盖；失重法测得的腐蚀速率随腐蚀时间延长呈现减小的趋势,并最终趋于稳定,与静止海水相比,流动海水中的腐蚀速率高出约1倍；电化学方法测得的腐蚀速率则随浸泡时间的延长而增大,与失重法的结果之间存在较为明显的偏差,并且浸泡时间越长,这一偏差越明显.长期浸泡后,碳钢表面的锈层对电化学测试结果产生影响,是导致电化学方法不能准确评估腐蚀速率的原因.
参考文献
| [1] | Javaherdashti R.Anti corros Methods Mater,2000; 47(1):30 |
| [2] | Zheng W L,Yu Q.Environment Sensitive Fraction of Steel.Beijing:Chemical Industry Press,1988:12(郑文龙,于青.钢的环境敏感断裂.北京:化学工业出版社,1988:12) |
| [3] | Zhu Y L,Zhou J,Xiong C J,Ma Z F,Liu Z S.Petrol Chem Equip,2002; 31(1):14(朱岳麟,周健,熊常健,马志锋,刘中生.石油化工设备,2002;31 (1):14) |
| [4] | Yan M,Huang G Q.Marine Sci,2005; 29(7):73 (颜民,黄桂桥.海洋科学,2005; 29(7):73) |
| [5] | Cao C N.Corrosion of Chinese Materials in Nature Environment.Beijing:Chemical Industry Press,2005:1(曹楚南.中国材料的自然环境腐蚀.北京:化学工业出版社,2005:1) |
| [6] | Xia L T,Huang G Q,Ding L P.Res Studies Foundry Equip,2002; 4:14(夏兰廷,黄桂桥,丁路平.铸造设备研究,2002;4:14) |
| [7] | Huang G Q.Corros Sci Prot Technol,2001; 13:81(黄桂桥.腐蚀科学与防护技术,2001; 13:81) |
| [8] | Qiu Y B,Qi G T,Guo Z H.China Offshore Oil Gas,1996;8(5):18(邱于兵,齐公台,郭稚弧.中国海上油气,1996; 8(5):18) |
| [9] | Zhang W,Wang J,Li Y N,Wang W.Acta Phys Chim Sin,2010;26:2941(张伟,王佳,李玉楠,王伟.物理化学学报,2010;26:2941) |
| [10] | Bousselmi L,Fiaud C,Tribollet B,Triki E.Electrochim Acta,1999; 44:4357 |
| [11] | John D G,Searosn P C,Dawson J L.Br Corros J,1981;16(2):102 |
| [12] | Liu G Z,Wang J M,Zhang J Q,Cao C N.Acta Metall Sin,2011; 47:1600(刘光洲,王建明,张鉴清,曹楚南.金属学报,2011; 47:1600) |
| [13] | Zhang J B,Wang J,Wang Y H.Acta Phys Chim Sin,2005; 21:993(张际标,王佳,王燕华.物理化学学报,2005; 21:993) |
| [14] | González J A,Miranda J M,Otero E,Feliu S.Corros Sci,2007; 49:436 |
| [15] | Zou Y,Zheng Y Y,Wang Y H,Wang J.Acta Metall Sin,2010; 46:123(邹妍,郑莹莹,王燕华,王佳.金属学报,2010; 46:123) |
| [16] | Zou Y,Wang J,Zheng Y Y.Acta Phys Chim Sin,2010;26:2361(邹妍,王佳,郑莹莹.物理化学学报,2010; 26:2361) |
| [17] | Zou Y,Wang J,Zheng Y Y.Corros Sci,2011; 53:208 |
| [18] | Antony H,Perrin S,Dillmann P,Legrand L,Chaussé A.Electrochim Acta,2007; 52:7754 |
| [19] | Andrade C,Keddam M,Nóvoa X R,Pérez M C,Rangel C M,Takenouti H.Electrochim Acta,2001; 46:3905 |
| [20] | Novák P,MaláR,Joska L.Cement Concrete Res,2001;31:589 |
| [21] | Copson H R.Corrosion,1960; 16:130 |
| [22] | Shalaby H M,Attari S,Riad W T.Corrosion,1992; 48:206 |
| [23] | Nesic S,Solvi G T,Enerhaug J.Corrosion,1995; 51:773 |
| [24] | Huang G Q.Corros Sci Prot Technol,2001; 22:384(黄桂桥.腐蚀科学与防护技术,2001; 22:384) |
| [25] | Martinez S.Mater Chem Phys,2002; 77:97 |
| [26] | Stern M,Geary A L.J Electrochem Soc,1957; 104:56 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%