层片状珠光体奥氏体化过程相对于球化珠光体的奥氏体化更复杂,由于沿垂直片层方向和沿片层方向的长大速率不同,需将奥氏体长大沿这2个方向分别处理.利用Thermo Calc软件计算初始组织的平衡成分,建立单片层模型.通过DICTRA软件模拟垂直片层方向长大的规律,对比垂直方向长大的抛物线规律,推算Fe-C-M(M=Mn,Cr)合金体系奥氏体化的抛物线生长速率系数.在沿片层方向,通过简化近似,并基于组织形貌观察结果,按照抛物线状界面假设构建长大模型.针对Fe-C二元合金推导了沿片层方向长大的一般式,并对界面形状进行修正.当假定界面形状达到稳定抛物线形状,可以通过观察组织形貌得到抛物线因子p和片层厚度λ,代入一般式确定沿片层长大速率.此外综合考虑界面能的影响,定性阐释了对称抛物线状界面的形成原因.
参考文献
| [1] | Mehl R,Hagel W.Prog Met Sci Phys,1956; 6:74 |
| [2] | Ko T,Cottrell S A.J Iron Steel Inst,1952; 172:307 |
| [3] | Greninger A B,Troiano A R.Trans AIME,1949; 185:590 |
| [4] | Krielaart G P,Sietsma J,Van der Zwaag S.Mater Sci Eng,1997; A237:216 |
| [5] | Roberts R A,Mehl R F.Trans ASM,1943; 31:613 |
| [6] | Brooks C R.Principles of the Austenitization of Steels.London:Elsevier Applied Science,1992:91 |
| [7] | Caballero F G,Capdevila C,García de Andrés C.ISIJ Int,2003; 43:726 |
| [8] | Akbay T,Reed R C,Atkinson C.Acta Metall Mater,1994;47:1469 |
| [9] | Miyamoto G,Usuki H,Li Z D,Furuhara T.Acta Mater,2010; 58:4492 |
| [10] | Akbay T,Atkinson C.J Mater Sci,1996; 31:2221 |
| [11] | Reed R C,Akbay T,Shen Z,Robinson J M,Root J H.Mater Sci Enq,1998; A256:152 |
| [12] | Park K T,Lee E G,Lee C S.ISIJ Int,2007,47:294 |
| [13] | Caballero F G,Capdevila C,De Andrés C G.J Mater Sci,2002; 37:3533 |
| [14] | Gaude-fugarolas D,Bhadeshia H K D H.J Mater Sci,2003; 38:1195 |
| [15] | Caballero F G,Capdevila C,De Andrés C G.Metall Mater Trans,2001; 32A:1283 |
| [16] | Rosz A,Gácsi Z,Fuchs E G.Acta Metall,1983; 31:509 |
| [17] | Speich G R,Szirmae A.Trans TMS-AIME,1969; 245:1063 |
| [18] | Li Z D,Miyamoto G,Yang Z G,Zhang Y D,Zhang C,Furuhara T.Acta Metall Sin,2010; 46:1066(李昭东,宫本吾郎,杨志刚,张玉朵,张弛,古原忠.金属学报,2010; 46:1066) |
| [19] | Karmazin L,KrejíJ.Mater Sci Eng,1994; A185:L5 |
| [20] | Hillert M,Nilsson K,Torndahl L E.JIron Steel Inst,1971;209:49 |
| [21] | Li Z D.PhD Dissertation,Beijing:Tsinghua University,2011(李昭东.北京:清华大学博士学位论文,2011) |
| [22] | Xia Y,Enomoto M,Yang Z G,Li Z D,Zhang C.Philos Mag,2012; 93:1095 |
| [23] | Atkinson C,Akbay T,Reed R C.Acta Metall Mater,1995;43:2013 |
| [24] | Coates D E.Metall Trans,1973; 4:395 |
| [25] | Atkinson C,Akbay T.Acta Mater,1996; 44:2861 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%