利用激光电子散斑干涉(ESPI)、电化学噪声(EN)及三维视频显微技术研究304不锈钢在3.5％NaCl溶液中点蚀早期单个蚀孔的发展动力学及其机理.结果表明在0.05V恒电位极化下,点蚀过程可分为4个阶段:首先,电流噪声在740s时发生剧烈波动,钝化膜开始破裂,点蚀孕育期为740s；其次,ESPI图像在750s时产生可见光斑,稳态蚀孔萌生期为10s；再次,750-780s时,蚀孔的发展速率不断增加,表明点蚀处于活性溶解期:最后,蚀孔生长速率迅速下降,发生钝化,而在793s后,由于出现次生蚀孔,生长速率再次上升.使用三维视频显微镜观察蚀孔形貌并测量蚀坑体积的变化,印证了由腐蚀产物浓度分析法得到的单个蚀孔的生长速率,并在蚀坑底部观察到了次生蚀孔.
参考文献
| [1] | Liao J X,Jiang Y M,Wu W W,Zhong C,Li J.Acta Metall Sin,2006;42:1187(廖家兴,蒋益明,吴玮巍,钟澄,李劲.金属学报,2006;42:1187) |
| [2] | Han D,Jiang Y M,Deng B,Zhang L H,Zhang W,Li J.Acta Metall Sin,2009;45:919(韩冬,蒋益明,邓博,张丽华,张伟,李劲.金属学报,2009;45:919) |
| [3] | Dong C F,Luo H,Xiao K,Sun T,Liu Q,Li X G.J Wuhan Univ Technol-Mater Sci,2011;26:641 |
| [4] | Li H B,Jiang Z H,Yang Y,Cao Y,Zhang Z R.J Metall Mater,2009;16:517 |
| [5] | Li G M,Guo X P,Zheng J S.J Iron Steel Res,2004;11(4):47 |
| [6] | Hu L H,Du N,Wang M F,Zhao Q.J Chin Soc Corros Prot,2007;27:233(胡丽华,杜楠,王梅丰,赵晴.中国腐蚀与防护学报,2007;27:233) |
| [7] | Hong J F,Tan H,Chen L D,Li J,Li L,Jiang Y M.Acta Metall Sin,2011;47:1445(洪巨峰,谭华,陈林豆,李劲,李莉,蒋益明.金属学报,2011;47:1445) |
| [8] | Tan Y J,Balley S,Kinsella B.Corros Sci,1996;38:1681 |
| [9] | Smulko J,Darouicki K.J Electroanal Chem,2003;545:59 |
| [10] | Wang M F,Du N,Li X G,Zhao Q,Liu G.Corros Prot,2009;30(1):29(王梅丰,杜楠,李晓刚,赵晴,刘刚.腐蚀与防护,2009;30(1):29) |
| [11] | Wang M F,Li X G,Du N,Huang Y Z,Korsunsky A.Electrochem Commun,2008;10:1000 |
| [12] | Pan Y,Zhang S P,Zhou J L,Li X G,Xiao Y D.Equip Environ Eng,2010;7(4):67(潘莹,张三平,周建龙,李晓刚,萧以德.装备环境工程,2010;7(4):67) |
| [13] | Lian C H,Gao Y.Chem Eng Mach,1995;22(2):87(梁成浩,高扬.化工机械,1995;22(2):87) |
| [14] | Ye T,Gao C Z.Mater Prot,2007;40(11):78(叶涛,高灿柱.材料保护,2007;40(11):78) |
| [15] | Liu G.Master Dissertation,Nanchang Hangkong Univ,2008(刘刚.南昌航空大学硕士学位论文,2008) |
| [16] | Pujar M G,Anita T,Shaikh H,Dayul R K,Khatak H S.J Mater Eng Perform,2007;16:494 |
| [17] | Jong J K.Met Mater Int,2011;17:777 |
| [18] | Du N,Huang L,Xu S,Wang L Q.Failure Anal Prev,2009;4:71(杜楠,黄乐,徐珊,王力强.失效分析与预防,2009;4:71) |
| [19] | Du N,Liu G,Zhao Q.Mater Sci,2008;2:326 |
| [20] | Jong J K.Met Mater Int,2009;15:279 |
| [21] | Girija S,Kamachi U,Mudali B R.Appl Electrochem,2011;41:973 |
| [22] | Yu Q B,Sun Y.Hot Work Technol,2010;39(2):1(于庆波,孙莹材料热处理技术,2010;39(2):1) |
| [23] | Chen Y F,Rairdan R,Luo J L.Appl Electrochem,1998;28:1371 |
| [24] | Zhang J Q,Zhang Z.J Chin Soc Corros Prot,2002;22:241(张鉴清,张昭.中国腐蚀与防护学报,2002;22:241) |
| [25] | Zhang Z,Zhang J Q.Chin J Nonferrous Met,2001;11:284(张昭,张鉴清.中国有色金属学报,2001:11:284) |
| [26] | Li L,Li X G,Dong C f,Cheng Y F.Corros Eng Sci Tech,2011;46:340 |
| [27] | Sun D M,Jiang Y M,Tang Y,Xiang Q W,Zhong C,Liao J X,Li J.Electrochim Acta,2009;54:1558 |
| [28] | Frankel G S.J Electrochem Soc,1998;145:2186 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%