根据等温条件下的铁素体晶粒长大公式,推导出了焊接热影响区(HAZ)铁素体晶粒长大的动力学方程,并结合焊接热循环的数值分析结果对TCS不锈钢热影响区晶粒长大进行了预测.在此基础上,对复合焊新型焊接工艺条件下TCS不锈钢HAZ的晶粒长大情况进行了数值计算,得到了3种工艺参数下TCS不锈钢复合焊HAZ内的晶粒尺寸.基于TCS不锈钢复合焊接接头的金相图片,测量了HAZ内的平均晶粒尺寸,对数值模拟结果进行了验证.初步讨论了晶粒尺寸随热循环温度的长大情况和热循环温度差异对晶粒长大的影响规律.
参考文献
| [1] | Du B,Sun J T,Xu Y J,Mao H,Jia Y L,Wang L X,Wang Z B,Zhang X B,Yu W,Liu Z C,Chen Z Y,Zhang Z C.Weld Join,2009; (1):1(杜兵,孙静涛,徐玉军,毛辉,贾玉力,王立新,王志斌,张心保,于维,刘志臣,陈增有,张志昌.焊接,2009:(1):1) |
| [2] | Li J L,Li J Q,Wu Y L,Huo L X,Zhang Y F.Weld Join,2007; (7):17(李加良,李践桥,武永亮,霍立兴,张玉风.焊接,2007;(7):17) |
| [3] | Dilthey U.Proc 8th Int Symposium on Innovations in Welding and Joining for a New Era in Manufacturing,Kyoto,Japan,2008:1 |
| [4] | Defalco J.Weld J,2007; 86:47 |
| [5] | Mo C L,Qian B N,Li D Z,Li J L.Chin J Mater Res,2001; 15:343(莫春立,钱百年,李殿中,李晶丽.材料研究学报,2001; 15:343) |
| [6] | Mo C L,Li D Z,Qian B N,Guo X M.Acta Metall Sin,2001; 37:307(莫春立,李殿中,钱百年,国旭明.金属学报,2001; 37:307) |
| [7] | Wu C S.Welding Thermal Processes and Weld Pool Behaviors.New York:CRC Press,2011; 47 |
| [8] | Cho J H,Na S J.J Phys,2006; 39D:5372 |
| [9] | Kaplan A.J Phys,1994; 27D:1805 |
| [10] | Xu G X,Wu C S,Qin G L,Wang X Y,Lin S Y.Acta Metall Sin,2008; 44:641(胥国祥,武传松,泰国梁,王旭友,林尚扬.金属学报,2008;44:641) |
| [11] | Xu G X,Wu C S,Qin G L,Wang X Y,Lin S Y.Acta Metall Sin,2009; 45:107(胥国祥,武传松,泰国梁,王旭友,林尚扬.金属学报,2009; 45:107) |
| [12] | Zhang Z Z,Xu G X,Wu C S.Acta Metall Sin,2011; 47:1450(张转转,胥国祥,武传松.金属学报,2011; 47:1450) |
| [13] | Wang L X,Song C J.Iron Steel,2008; 43:71(王立新,宋长江.钢铁,2008; 43:71) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%