采用Gleeble-1500热模拟机对GH738镍基高温合金进行了高温热压缩变形实验,分析了该合金在初始晶粒不同的情况下,变形温度1000-1160℃,应变速率0.01-10 s-1,工程变形量15%-70%条件下流变应力的变化规律及晶粒组织演化规律;同时研究了变形温度1040-1120℃,应变速率0.1-10 s-1,变形量15%-50%,保温时间0-45 s条件下该合金的亚动态(静态)再结晶及保温温度980-1140℃,保温时间0-4 h条件下的晶粒长大行为.通过系统的物理热模拟实验,构建了GH738高温合金在热变形过程中的晶粒组织演化模型及应力-应变模型,所建立的GH738高温合金模型与实验结果相比均表现出较高的相关度.
参考文献
[1] | Yao Z H,Dong J X,Zhang M C,Zheng L.Rare Met Mater Eng,2010; 39:1565(姚志浩,董建新,张麦仓,郑磊.稀有金属材料与工程,2010;39:1565) |
[2] | Chang K M,Liu X B.Mater Sci Eng,2001; A308:1 |
[3] | Semiatin S L,Fagin P N,Glavicic M G.Scr Mater,2004;50:625 |
[4] | Liu X B,Kang B,Chang K M.Mater Sci Eng,2003; A340:8 |
[5] | Yao Z H,Dong J X,Zhang M C,Yu Q Y,Zheng L.Trans Mater Heat Treat,2011; 32:44(姚志浩,董建新,张麦仓,于秋颖,郑磊.材料热处理学报,2011:32:44) |
[6] | Donachie M J,Pinkowish A A,Danesi W P,Radavich J F,Couts W H.Metall Trans,1970; 1:2623 |
[7] | Guimaraes A A,Jonas J J.Metall Trans,1981; A12:1655 |
[8] | Livesey D W,Sellars C M.Mater Sci Technol,1985; 1:136 |
[9] | Li M Q,Yao X Y,Luo J,Lin Y Y,Su S B,Wang H R.Acta Metall Sin,2007; 43:937(李淼泉,姚晓燕,罗皎,林莺莺,苏少博,王海荣.金属学报,2007; 43:937) |
[10] | Salehi A R,Serajzadeh S,Yazdipour N.Mater Chem Phys,2007; 101:153 |
[11] | Gao H,Barber G C,Chen Q A,Lu Y Q.J Mater Process Technol,2003; 142:52 |
[12] | Ganapathysubramanian S,Zabaras N.Int J Solid Struct,2004; 41:2011 |
[13] | Wang B X,Liu X H,Wang G D.Mater Sci Eng,2005;A393:102 |
[14] | Sui F L,Xu L X,Chen L Q,Liu X H.J Mater Process Technol,2011; 211:433 |
[15] | Zhao M L,Sun W R,Yang S L,Qi F,Guo S R,Hu Z Q.Acta Metall Sin,2009; 45:79(赵美兰,孙文儒,杨树林,祁峰,郭守仁,胡壮麒.金属学报,2009; 45:79) |
[16] | Sellars C M,McTegart W J.Acta Metall,1966; 14:1136 |
[17] | McQueen H J,Ryan N D.Mater Sci Eng,2002; A322:43 |
[18] | Sommitsch C,Mitter W.Acta Metall,2006; 54:357 |
[19] | Gottstein G,Frommert M,Goerdeler M,Schafer N.Mater Sci Eng,2004; A387-389:604 |
[20] | Solhjoo S.Mater Des,2010; 31:1360 |
[21] | Poliak E I,Jonas J J.ISIJ Int,2003; 43:692 |
[22] | Li G,Maccagno T M,Bai D Q.ISIJ Int,1996; 36:1479 |
[23] | Bai D Q,Yue S,Jonas J J.ISIJ Int,1996; 36:1084 |
[24] | Shen B Z,Fang N W,Shen H F,Liu B C.Mater Sci Technol,2005; 13:516(沈丙振,方能炜,沈厚发,柳百成.材料科学与工艺,2005; 13:516) |
[25] | Li G,Maccagno T M,Bai D Q.ISIJ Int,1996; 36:1479 |
[26] | Sellars C M,Whiteman J A.Met Sci,1979; 13:187 |
[27] | Anelli E.ISIJ Int,1992; 32:440 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%