相同热处理后4不同N含量Inconel 690合金(Ni-30Cr-10Fe-xN (x=0.001,0.011,0.018,0.030,质量分数,%))晶界M23C6析出形貌和Cr贫化存在明显差异,N在晶界有明显偏聚行为.随着N含量的增加,TiN析出量和退火孪晶增多,TT处理后晶界析出的碳化物细小而离散,晶界Cr贫化得到改善.室温拉伸结果表明,N含量由0.001%增加到0.030%时,合金室温屈服强度和抗拉强度均提高约50 MPa,而延伸率和断面收缩率仅稍有降低.含N合金断裂方式均为韧性断裂,韧窝尺寸随N含量增加而减小.
参考文献
[1] | Kai J J,Liu M N.Scr Metall,1989; 23:17 |
[2] | Sarver J M,Crum J R,Mankins W L.Corros NACE,1988;44:288 |
[3] | Fuchs G E,Haydon S Z.Scr Metall Mater,1991; 25:1483 |
[4] | Kai J J,Tsai C H,Huang T A,Liu M N.Metall Trans,1989; 20A:1077 |
[5] | Dutta R S,Tewari R,De P K.Corros Sci,2007; 49:303 |
[6] | Zhu H,Dong J X,Zhang M C,Hu Y H,Xie X S.J Univ Sci Technol Beijing,2002; 24:511(朱红,董建新,张麦仓,胡尧和,谢锡善.北京科技大学学报,2002; 24:511) |
[7] | Lu Y,Qin X B.Boiler Manufactur,1994; 154:54(鲁悦,秦绪斌.锅炉制造,1994; 154:54) |
[8] | Mudali U K,Baldev R,Translated by Li J,Huang Y H. High Nitrogen Steels and Stainless SteelsManufacturing, Properties and Applications. Beijing:Chemical Industry Press,2006:48(Mudali U K,Baldev R著;李晶,黄运华译.高氮钢和不锈钢—生产,性能与应用.北京:化学工业出版社,2006:48) |
[9] | Simmons J W.Mater Sci Eng,1996; A207:159 |
[10] | Reed R P.JOM,1989; 3:16 |
[11] | Rhodes G O,Conway J J.JOM,1996; 4:28 |
[12] | Levey P R,van Bennekom A.Corrosion,1995; 51:911 |
[13] | Thuvander M,Stiller K,Olsson E.Mater Sci Technol,1999; 15:237 |
[14] | Liu K,Hao X C,Gao M,Li S,Li Y Y,Wan B F.Proc 17th Int Conf Nuclear Engineering,Three Park Avenue,New York,2010 (CD-ROM) |
[15] | Dutta R S,Lobo A,Purandare R,Kulkarni S K,Dey G K.Metall Mater Trans,2002; 33A:1437 |
[16] | Meng F J,Wang J Q,Han E H,Ke W.Corros Sci,2010;52:927 |
[17] | Abdulranhan R F,Hendry A.Metall Mater Trans,2001;32B:1103 |
[18] | Mitchell A.Acta Metall Sin (Engl Lett),2005; 18:575 |
[19] | Simmons J W,Covino B S,Hawk J A.ISIJ Int,1996; 36:846 |
[20] | Degallaix S,Foct J,Hendry A.Mater Sci Technol,1986;2:946 |
[21] | Pande C S,Rath B B,Imam M A.Mater Sci Eng,2004;A367:171 |
[22] | Pande C S,Imam M A.Mater Sci Eng,2009; A512:82 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%