为抑制合金元素的互扩散,在Ni-Cr-Al-Y-Si涂层和DSM11基体间通过电弧离子镀技术一步制备了含扩散阻挡层(DB)和黏结层(BC)的多层体系Ni-Cr-Al-Y-Si/DB/BC/DSM11.由恒温氧化,循环氧化和粘胶拉伸实验考察了涂层的抗氧化性、DB阻挡元素扩散能力和体系的界面结合强度.结果表明,含扩散阻挡层的多层能很好地保护基体材料,经过1050℃恒温氧化100 h后,试样表面形成连续致密的Al2O3膜,外层中仅检测到微量的来自基体的合金元素;经过1050℃≒室温(RT)循环氧化100 cyc后,DB与两侧材料的结合保持良好.退火多层体系的界面结合强度达到63.6 MPa,比不连续法制备的Ni-Cr-Al-Y/Cr-O-N/DSM11体系提高了约20 MPa.一步法制备能提高含扩散阻挡层多层体系的界面结合强度,DB在恒温和循环氧化过程中能保持很好的抑制元素扩散的能力.
参考文献
| [1] | Knotek O,Loftier F,Beele W.Surf Coat Technol,1993;61:6 |
| [2] | Li S S,Song J X,Zhou C G,Gong S K,Han Y F.Inter-metallics,2005; 13:309 |
| [3] | Sloof W G.Self Healing in Coating at High Temperatures:Self Healing Materials.Netherlands:Springer,2007:309 |
| [4] | Nicholls J R.MRS Bull,2003; 28:659 |
| [5] | Wang Q M,Wu Y N,Ji A L,Ke P L,Sun C,Huang R F,Wen L S.Acta Metall Sin,2004; 40:83(王启民,武颖娜,纪爱玲,柯培玲,孙超,黄荣芳,闻立时.金属学报,2004;40:83) |
| [6] | Li W Z,Yao Y,Wang Q M,Bao Z B,Gong J,Sun C,Jiang X.J Mater Res,2008; 23:341 |
| [7] | Li W Z,Yao Y,Li Y Q,Li J B,Gong J,Sun C,Jiang X.Mater Sci Eng,2009; A512:117 |
| [8] | Yao Y,Li W Z,Wang Q M,Gong J,Sun C,Li J B.ActaMetall Sin,2008;44:876(姚勇,李伟洲,王启民,宫骏,孙超,李家宝.金属学报,2008;44:876) |
| [9] | Zhang K,Wang Q M,Sun C,Wang F H.Corros Sci,2008;50:1707 |
| [10] | Sun C,Wang Q M,Tang Y J,Guan Q F,Gong J,Wen L S.Acta Metall Sin,2005; 41:1167(孙超,王启民,唐永吉,关庆丰,宫骏,闻立时.金属学报.2005;41:1167) |
| [11] | Ren X,Wang F H.Surf Coat Technol,2006; 201:30 |
| [12] | Yao Y.Master Dissertation.Institute of Metal Research,Chinese Academy of Sciences,Shenyang,2008(姚勇.中国科学院金属研究所硕士学位论文,沈阳,2008) |
| [13] | Peng X,Wang F H,Clark D K.Acta Metall Sin,2003; 39:1055(彭晓,王福会,Clarke D R.金属学报.2003;39:1055) |
| [14] | Cremer R,Witthaut M,Reichert K,Schierling M,Neusch(u)tz D.Surf Coat Technol,1998; 108-109:48 |
| [15] | Xie L,Sohn Y,Jordan E H,Gell M.Surf Coat Technol,2003; 176:57 |
| [16] | Evans A G,Mumm D R,Hutchinson J W,Meier G H,Pettit F S.Prog Mater Sci,2001; 46:505 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%